Transition metal complexes, catalyst compositions containing the same, and olefin polymerization using the catalyst compositions

ABSTRACT

Provided are a novel transition metal complex where a monocyclopentadienyl ligand to which an amido or alcoxy group is introduced is coordinated, a method of synthesizing the same, and olefin polymerization using the transition metal complex. Compared to a conventional transition metal complex having a silicon bridge and an oxido ligand, the transition metal complex has a phenylene bridge, so that a monomer easily approaches the transition metal complex in terms of structure and a pentagon ring structure of the transition metal complex is stably maintained. The catalyst composition including the transition metal complex is used to synthesize a polyolefin copolymer having a very low density less than 0.910 g/cc.

CROSS-REFERENCE TO RELATED PATENT APPLICATIONS

This application claims the benefit of Korean Patent Application No. 10-2005-0061820, filed on Jul. 8, 2005, in the Korean Intellectual Property Office, the disclosure of which is incorporated herein in its entirety by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a novel transition metal complex where a monocyclopentadienyl ligand to which an amido or alcoxy group is introduced is coordinated, a method of synthesizing the same, and olefin polymerization using the transition metal complex, and more particularly, to a novel transition metal complex containing a phenylene bridge, a method of synthesizing the same, and olefin polymerization using the transition metal complex.

2. Description of the Related Art

In the early 1990s, Dow Co. developed Me₂Si(Me₄C₅)(NtBu)TiCl₂ (Constrained-Geometry Catalyst, hereinafter referred to as CGC) (U.S. Pat. No. 5,064,802). CGC shows excellent properties in a copolymerization reaction of ethylene and alpha-olefin, compared to conventional metallocene catalysts. For example, (1) CGC can be used to form high molecular weight polymers due to its high reactivity at high polymerization temperature, and (2) CGC can be used for copolymerization of alpha-olefin having large steric hindrance, such as 1-hexene and 1-octene. Due to many useful properties, in addition to these properties described above, obtained from use of CGC, research into synthesis of CGC derivatives as a polymerization catalyst is substantially increasing in academic and industrial fields.

For example, synthesis of metal complexes comprising other various bridges instead of a silicon bridged CGC and containing a nitrogen substituent, and polymerization using these metal complexes were performed. Examples of such metal compounds include Complexes 1 through 4 (Chem. Rev. 2003, 103, 283).

Complexes 1 through 4 respectively contain a phosphorus bridge, an ethylene or propylene bridge, a methyllidene bridge, and a methylene bridge, instead of the silicon bridge of the CGC structure. However, these complexes show low activity or poor copolymerization performance when ethylene is polymerized or when ethylene and alpha-olefin are copolymerized, compared to CGC.

In addition, the amino ligand in CGC can be replaced with an oxido ligand. some of such complexes were used for polymerization. Examples of such complexes include:

In Complex 5, which was developed by T. J. Marks et al., a cyclopentadiene (Cp) derivative is bridged to an oxido ligand by ortho-penylene group (Organometallics 1997, 16, 5958). A complex having the same bridge and polymerization using the compound were suggested by Mu et al. (Organometallics 2004, 23, 540). A complex in which an indenyl ligand is bridged to an oxido ligand by an ortho-phenylene group was developed by Rothwell et al. (Chem. Commun. 2003, 1034). In Complex 6, which was developed by Whitby et al., a cyclopentadienyl ligand is bridged to an oxido ligand by three carbon atoms (Organometallics 1999, 18, 348). It was reported that Complex 6 showed reactivity in syndiotactic polystyrene polymerization. Similar complexes to Complex 6 were developed by Hessen et al. (Organometallics 1998, 17, 1652). Complex 7, which was developed by Rau et al., showed reactivity when being used for ethylene polymerization and ethylene/1-hexen copolymerization at high temperature and high pressure (210° C., 150 Mpa) (J. Organomet. Chem. 2000, 608, 71). Complex 8, which has a similar structure to Complex 7, can be used for high temperature, high pressure polymerization, which was applied to US Patent Office by Sumitomo Co. (U.S. Pat. No. 6,548,686).

However, only some of these catalysts described above are used in commercial industry. Accordingly, there is still a need to develop a catalyst inducing high polymerization performance.

SUMMARY OF THE INVENTION

The present invention provides a novel transition metal complex having a phenylene bridge.

The present invention also provides a novel organic amine-based compound.

The present invention also provides a novel organic ketone-based boronic acid compound.

The present invention also provides a method of preparing the transition metal complex.

The present invention also provides a catalyst composition containing the transition metal complex.

The present invention also provides a method of preparing the catalyst composition.

The present invention also provides a method of preparing a polymer using the catalyst composition.

The present invention also provides a polymer prepared using the method of preparing a polymer using the catalyst composition.

According to an aspect of the present invention, there is provided a transition metal complex of Formula 1:

where R₁ and R₂ are each independently a hydrogen atom; a C1-C20 alkyl, aryl, or silyl radical; a C1-C20 alkenyl, alkylaryl, or arylalkyl radical; or a metalloid radical of Group 14 metal substituted with hydrocarbyl, wherein R₁ and R₂ can be connected by an alkylidine radical that contains a C1-C20 alkyl or aryl radical to form a ring;

R₄ is each independently a hydrogen atom; a halogen radical; or a C1-C20 alkyl or aryl radical, wherein two R₄ are connected to form a fused ring structure;

R₃ is a C1-C20 alkyl sulfonyl, aryl sulfonyl, or silyl sulfonyl radical; a C1-C20 alkyl carbonyl, aryl carbonyl, or silyl carbonyl radical; C1-C20 alkyl carboxy, or aryl carboxy radical; or C1-C20 alkyl phosphonyl, or aryl phosphonyl radical;

M is a transition metal of Group 4; and

Q₁ and Q₂ are each independently a halogen radical; a C1-C20 alkyl or aryl amido radical; a C1-C20 alkyl, alkenyl, aryl, alkylaryl, or arylalkyl radical; or a C1-C20 alkylidene radical.

The transition metal complex of Formula 1 may be represented by Formula 14:

where R₁₁ and R₁₂ are each independently hydrogen atom; or C1-C20 alkyl, aryl, or silyl radical;

R₁₄ is each independently hydrogen atom; a C1-C20 alkyl radical; or halogen radical;

Q₃ and Q₄ are each independently a halogen radical; C1-C20 alkyl, or aryl amido radical; or C1-C20 alkyl radical;

M is a transition metal of Group 4; and

where Y is a carbon atom or a sulfur atom;

R₉ is a hydrogen atom; a C1-C20 alkyl, aryl, or silyl radical; or a C1-C20 alcoxy, or aryloxy radical; and

when Y is the carbon atom, n is 1, and when Y is the sulfur atom, n is 2.

The transition metal complex of formula 1 may be represented by one of formulae below:

where R₁₀ is methyl, tosyl, mesityl, or t-butyl radical; Q₅ and Q₆ are each independently methyl a dimethylamido radical or a chloride radical.

According to another aspect of the present invention, there is provided a transition metal complex of Formula 2:

where R₁, R₂, R₄, M, Q₁ and Q₂ are described above;

G is an oxygen atom or a sulfur atom; and

R₅ is a hydrogen atom; a C1-C20 alkyl or aryl radical; or a C1-C20 alcoxy or aryloxy radical.

According to another aspect of the present invention, there is provided a transition metal complex of Formula 3:

where R₁, R₂, R₄, R₅, M, Q₁, and Q₂ are described above; and G′ is an oxygen atom, a sulfur atom, or a substituted nitrogen group (—NR) where R is a C1-C20 alkyl or aryl radical.

The transition metal complexes of formula 2 or formula 3 may be represented by:

where R₁₁, R₁₂, R₁₄, Q₃, Q₄, M, and R₅ are described above, and G″ is an oxygen atom, a sulfur atom, or a substituted nitrogen group where a subsituent is a C1-C20 alkyl or aryl amido radical.

The transition metal complexes of formula 2 or formula 3 may be represented by one of formulae below:

where R₁₅ is methyl radical, t-butyl radical, or t-butoxy radical; Q₅ and Q₆ are described above; and X is a halogen radical.

According to another aspect of the present invention, there is provided amine-based compounds of Formulae 4 through Formula 7:

where R₁, R₂, R₃, and R₄ are described above.

According to another aspect of the present invention, there is provided an organic ketone-based boronic acid compound of Formula 8:

where R₁ and R₂ are described above.

According to another aspect of the present invention, there is provided a method of synthesizing a transition metal complex, the method including:

synthesizing a compound of Formula 6 by reacting a boronic acid compound of Formula 8 with a 2-bromoaniline compound of Formula 9;

synthesizing a compound of Formula 5 by the compound of Formula 6 with R₃X where X is a halogen atom;

synthesizing a compound of Formula 4 by reacting a compound of Formula 5 with R₁Li and then adding an acid thereto; and

synthesizing a complex of Formula 1 or Formula 2 by reacting the comound of Formula 4 with the compound of Formula 10 and then adding (CH₃)_(n)SiX_(4-n) where X is a halogen atom and n is 0, 1, 2, or 3 thereto:

where R₄ is each independently a hydrogen atom; a halogen radical; or a C1-C20 alkyl or aryl radical, wherein two R₄ are connected to form a fused ring structure; and M(N(R₆)₂)₄   (10) where M is a transition metal of Group 4, and

R₆ is a C1-C20 alkyl or aryl radical.

According to another aspect of the present invention, there is provided a method of synthesizing a transition metal complex, the method including:

synthesizing a compound of Formula 6 by reacting a boronic acid compound of Formula 8 with a 2-bromoaniline compound of Formula 9;

synthesizing a compound of Formula 7 by the compound of Formula 6 with R₁Li and then adding an acid thereto;

synthesizing a compound of Formula 4 by reacting a compound of Formula 7 with R₃X where X is a halogen atom; and

synthesizing a complex of Formula 1 or Formula 2 by reacting the comound of Formula 4 with the compound of Formula 10 and then adding (CH₃)_(n)SiX_(4-n) where X is a halogen atom and n is 0, 1, 2, or 3 thereto.

According to another aspect of the present invention, there is provided a method of synthesizing a transition metal complex, the method comprising:

synthesizing a dilithium form of the compound of Formula 7 by reacting a compound of Formula 7 with an alkyllihtium that is a base; and

synthesizing a complex of Formula 3 by reacting an in-situe mixture composed of the dilithium compound, alkyllithium, and MX₄ where X is halogen and M is a transition metal of Group 4.

According to another aspect of the present invention, there is provided catalyst composition including:

the transition metal complex of any one of formulaes 1, 2, and 3; and

at least one cocatalyst compound selected from compounds of Formulae 11 through 13: —[Al(R₇)—O]_(a)—  (11) where R₇ is each independently a halogen radical; a C1-C20 hydrocarbyl radical; or a C1-C20 hydrocarbyl radical substituted with halogen; and

a is an integer of 2 or greater; D(R₇)₃   (12) where D is aluminum or borone; and R₇ is described above; and [L-H]⁺[Z(A)₄]⁻, or [L]⁺[Z(A)₄]⁻  (13) where L is a neutral or cationic Lewis acid;

H is a hydrogen atom;

Z is an elemnet of Group 13;

A is each independently a C6-C20 aryl or alkyl radical in which at least one hydrogen atom is substituted with halogen or a C1-C20 hydrocarbyl, alcoxy, or phenoxy radical.

According to another aspect of the present invention, there is provided a method of preparing a catalyst composition, the method including:

contacting the transition metal complex of any one of formulaes 1, 2, and 3 with the compound of Formula 11 or Formula 12, thereby obtaining a mixture; and

adding a compound of Formula 13 to the mixture.

The mole ratio of the transition metal complex to the compound of Formula 11 or Formula 12 may be in the range of 1:2 through 1:5000, and the mole ratio of the transition metal complex of the compound of Formula 13 may be in the range of 1:1 through 1:25.

According to another aspect of the present invention, there is provided a method of synthesizing an olefin polymer, including contacting the catalyst composition with a monomer.

The monomer may contain at least one monomer selected from the group consisting of ethylene, propylene, 1-butene, 1-pentene, 4-methyl-1-pentene, 1-hexene, 1-hepthene, 1-octene, 1-decene, 1-undecene, 1-dodecene, 1-tetradecene, 1-hexadecene, and 1-itosen.

According to another aspect of the present invention, there is provided an olefin polymer synthesized using the method of synthesizing an olefin polymer.

The monomer that is used to synthesize the olefin polymer may include: ethylene; and at least one compound selected from the group consisting of propylene, 1-butene, 1-hexene, 4-methyl-1-pentene, and 1-octene.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other features and advantages of the present invention will become more apparent by describing in detail exemplary embodiments thereof with reference to the attached drawings in which:

FIG. 1 illustrates an X-ray structure of (p-toluenesulfonylamido)(2,5-dimethylcyclopentadienyl)titanium bis(dimethylamide) that is a transition metal complex according to an embodiment of the present invention;

FIG. 2 illustrates an X-ray structure of 4,6-difluorophenylene(t-butyliminooxy)(2,5-dimethylcyclopentadienyl)-titanium dichloride that is a transition metal complex according to another embodiment of the present invention; and

FIG. 3 illustrates an X-ray structure of phenylene(t-butylcarboxamido)(2,5-dimethylcyclopentadienyl)titanium dimethyl that is a transition metal complex according to another embodiment of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

The present invention will now be described more fully with reference to the accompanying drawings.

A transition metal complex according to an embodiment of the present invention has a phenylene bridge, so that a sterically hindered monomer easily approaches the transition metal complex and a pentagon ring structure of the transition metal complex is stably maintained, compared to a conventional transition metal complex having a silicon bridge and an oxido ligand. By using a catalyst composition including the transition metal complex according to an embodiment of the present invention, a polyolefin copolymer having a very low density less than 0.910 g/cc can be obtained.

A transition metal complex according to an embodiment of the present invention may be represented by Formula 1:

where R₁ and R₂ are each independently a hydrogen atom; a C1-C20 alkyl, aryl, or silyl radical; a C1-C20 alkenyl, alkylaryl, or arylalkyl radical; or a metalloid radical of Group 14 metal substituted with hydrocarbyl, wherein R₁ and R₂ can be connected by an alkylidine radical that contains a C1-C20 alkyl or aryl radical to form a ring; R₄ is each independently a hydrogen atom; a halogen radical; or a C1-C20 alkyl or aryl radical, wherein two R₄ can be connected to form a fused ring structure; R₃ is a C1-C20 alkyl sulfonyl, aryl sulfonyl, or silyl sulfonyl radical; a C1-C20 alkyl carbonyl, aryl carbonyl, or silyl carbonyl radical; C1-C20 alkyl carboxy, or aryl carboxy radical; or C1-C20 alkyl phosphonyl, or aryl phosphonyl radical; M is a transition metal of Group 4; and Q₁ and Q₂ are each independently a halogen radical; a C1-C20 alkyl or aryl amido radical; a C1-C20 alkyl, alkenyl, aryl, alkylaryl, or arylalkyl radical; or a C1-C20 alkylidene radical.

In the transition metal complex of Formula 1 according to an embodiment of the present invention, a cyclopentadienyl derivative is connected to an amido group by a phenylene bridge such that a Cp-M-N angle is small but a Q₁-M-Q₂ angle to which a monomer approachs is large, which is illustrated in FIG. 1. In addition, compared to a CGC structure that includes a silicon bridge, the complex of Formula 1 has a stable, strong pentagon ring where Cp, a phenylene bridge, and nitrogen are connected to a metal site. Accordingly, when the complex of Formula 1 which is activated by a cocatalyst, such as methylaluminoxane, or B(C₆F₅)₃, is applied to the synthesis of polyolefin, a polyolefin with high molecular weight, and high degree of copolymerization an be obtained even at high reaction temperature. Due to such structural feature of the complex of Formula 1, a linear low density polyethylene having a density of 0.910-0.930 g/cc. In addition, since a great amount of alpha-olefin can be comprised, a polyolefin copolymer having a very low density less than 0.910 g/cc can be obtained. In addition, various substituents can be introduced to a cyclopentadienyl ring, nitrogen, and a phenylene ring so that electronic and steric environments in the vicinity of metal can be easily controlled to obtain desired structure and properties of a polymer which will be formed. The transition metal complex according to an embodiment of the present invention is used to prepare a catalyst that is used to polymerize olefin monomers. However, use of the transition metal complex is not limited thereto, that is, the transition metal complex can be used in any application to which the transition metal complex can be used.

The compound of Formula 1 may have the structure corresponding to Formula 14, which is preferred to control electronic, steric environments in the vicinity of metal:

where R₁₁ and R₁₂ are each independently hydrogen atom; or C1-C20 alkyl, aryl, or silyl radical;

R₁₄ is each independently hydrogen atom; a C1-C20 alkyl radical; or halogen radical;

Q₃ and Q₄ are each independently a halogen radical; C1-C20 alkyl, or aryl amido radical; or C1-C20 alkyl radical;

M is a transition metal of Group 4; and

where Y is a carbon atom or a sulfur atom;

R₉ is a hydrogen atom; a C1-C20 alkyl, aryl, or silyl radical; or a C1-C20 alcoxy, or aryloxy radical; and

when Y is the carbon atom, n is 1, and when Y is the sulfur atom, n is 2.

The transition metal complex of Formula 1 may be a compound of one of the formulae below:

where R₁₀ is a methyl radical, a tosyl radical, a mesityl radical, or t-butyl radical; Q₅ and Q₆ are each independently a methyl radical, a dimethylamido radical, or a chloride radical.

Transition metal complexes according to another embodiment of the present invention are represented by Formulae 2 and 3 where N or G, which is a hetroatom, are bound to metal. These transition metal complexes may have a chemical structure of η ¹-G bonding mode (Formula 2) or η ²-N,G bonding mode (Formula 3), accoridng to a substituent of a cyclopentadienyl ring or phenylene bridge, or a method of synthesizing a complex. Structures of these complexes are illustrated in FIGS. 2 and 3:

where R₁, R₂, R₄, M, Q₁ and Q₂ are described above; G is an oxygen atom or a sulfur atom; and R₅ is a hydrogen atom; a C1-C20 alkyl or aryl radical; or a C1-C20 alcoxy or aryloxy radical. <Formula 3>

where R₁, R₂, R₄, R₅, M, Q₁, and Q₂ are described above; and G′ is an oxygen atom, a sulfur atom, or a substituted nitrogen group (—NR) where R is a C1-C20 alkyl or aryl radical. These transition metal complexes according to another embodiment of the present invention are used to prepare a catalyst that is used to polymerize olefin monomers. However, use of these transition metal complexes is not limited thereto, that is, the transition metal complexes can be used in any application to which the transition metal complex can be used.

The transition metal complex of Formula 2 or Formula 3 may have the structure corresponding to Formula 16, which is preferred to control electronic, steric environments in the vicinity of metal:

where R₁₁ and R₁₂ are each independently hydrogen atom; or C1-C20 alkyl, aryl, or silyl radical;

R₁₄ is each independently a hydrogen atom; a C1-C20 alkyl radical; or a halogen radical;

Q₃ and Q₄ are each independently a halogen radical; a C1-C20 alkyl or aryl amido radical; or a C1-C20 alkyl radical;

M and R₅ are described above; and

G″ is a oxygen atom, a sulfur atom, or a substituted nitrogen group where a subsituent is a C1-C20 alkyl or aryl amido radical.

The transition metal complex of Formula 2 or Formula 3 may be a compound of any one of the formulae below:

where R₁₅ is a methyl, t-butyl, or t-butoxy radical, and Q₅ and Q₆ are described above, and X is a halogen radical.

The present invention also provides amine-based compounds of Formulae 4 through 7 that are ligands coordinated with metal in the transition metal complex of Formulae 1 through 3:

where R₁, R₂, R₃ and R₄ are described above. When these ligands are coordinated with metal, a phenylene bridge is formed and nitrogen and cyclopentadiene are coordinated with metal. These compounds of Formulae 4 through 7 may be used as a ligand of a transition metal complex. However, use of the compounds is not limited thereto. That is, the compounds can be used in any applications.

The present invention also provides an organic ketone-based boronic acid compound of Formula 8 that is used as an intermediate when the ligands described above are synthesized:

<Formula 8>

where R₁ and R₂ are described above.

A method of preparing transition metal complexes of Formulae 1 through 3 according to an embodiment of the present invention will now be described in detail. In order to obtain a novel monocyclopentadienyl ligand in which phenylene of Formula 4 acts as a bridge, a substituted boronic acid is reacted with an aniline compound in the presence of Pd metal catalyst by carbon-carbon coupling, which is Suzuki Reaction. The Suzuki Reaction is well known in the organic chemistry to form a C—C bond, and can be used to synthesize a monocyclopentadienyl ligand of Formula 4 in which various substituents are introduced to cyclopentadienyl, nitrogen, and a phenylene bridge. Ultimately, the transition metal complex of Formula 1 in which electronic and steric hindrance is controlled in the vicinity of metal can be synthesized.

Particularly, the method of synthesizing transition metal complexes represented by Formulae 1 through 3 includes: a) synthesizing a compound of Formula 6 by reacting a boronic acid compound of Formula 8 with a 2-bromoaniline compound of Formula 9; b) synthesizing a compound of Formula 5 by the compound of Formula 6 with R₃X where X is a halogen atom; c) synthesizing a compound of Formula 4 by reacting a compound of Formula 5 with R₁Li and then adding an acid thereto; and d) synthesizing a complex of Formula 1 or Formula 2 by reacting the comound of Formula 4 with the compound of Formula 10 and then adding (CH₃)_(n)SiX_(4-n) where X is a halogen atom and n is 0, 1, 2, or 3 thereto:

where R₄ is described above; and M(N(R₆)₂)₄   (10) where M is a transition metal of Group 4, and

R₆ is a C1-C20 alkyl or aryl radical.

In operation (a), the boronic acid compound of Formula 8 can be obtained by reacting an unsaturated keton compound with a boron triester compound in a solvent of THF or ether and then adding an acid thereto, and the boronic acid compound of Formula 8 is reacted with a boromoaniline compound in the presence of a palladium catalyst via Suzuki Coupling reaction to form an amine-based compound of Formula 6. The palladium catalyst used can be a phosphine-based complex of Formula 11 which is well known. For example, the palladium catalyst is tetrakis(triphenylphosphine)palladium.

where R is alkyl or aryl; and X is a halogen atom.

In operation (b), a compound of Formula 6 is reacted with R₃—X where X is a halogen atom in the presence of an amine-based base, such as pylidine or triethylamin so that an acid such as H—X is removed and a compound of Formula 5 can be obtained. In the R₃—X, R₃ is selected from a C1-C20 alkyl sulfonyl or aryl sulfonyl radical, a C1-C20 alkyl carbonyl or aryl carbonyl radical, a C1-C20 alkyl carboxy or aryl carboxy radical, and a C1-C20 alkyl phosphonyl or aryl phosphonyl radical, and is preferably selected from methylsulfonyl, toluenesulfonyl, mesitylsulfonyl, and t-butylcarbonyl.

In operation (c), a compound of Formula 5 is reacted with an R₁Li compound at low temperature and then an acid treatment is performed, thereby obtaining a compound of Formula 4. In order to increase the reactivity of the R₁Li compound, the R₁Li compound can be used together with a metal Lewis acid such as CeCl₃. In the R₁Li compound, R₁ is selected from a C1-C20 alkyl or aryl; a C1-C20 alkenyl, alkylaryl, or arylalkyl; and a metalloid radical of Group 14 metal substituted with hydrocarbyl, preferably is a C1-C10 alkyl or aryl radical, and more preferably is selected from methyl, t-butyl, phenyl, benzyl, and (trimethyl)silylmethyl.

In operation (d), the monocyclopentadienyl ligand of Formula 4 prepared above is reacted with a Group 4 metal amino compound of Formula 10, and then (CH₃)_(n)SiX_(4-n) where X is halogen and n is 0, 2, or 3 is added thereto, thereby obtaining Group 4 transition metal complexes of Formulae 1 through 3 accoridng to the ligand structure change. The Group 4 metal a

mino compound is selected from tetrakis(dimethylamino)titanium, tetrakis(diethylamino)titanium, tetrakis(dimethylamino)zirconium, tetrakis(diethylamino)zirconium, tetrakis(dimethylamino)hafnium, and tetrakis(diethylamino)hafnium, and preferably selected from tetrakis(dimethylamino)titanium, tetrakis(dimethylamino)zirconium, and tetrakis(dimethylamino)hafnium. The reaction temperature of the monocyclopentadienyl ligand with the Group 4 metal amino compound may be in the range of 30° C.-150° C., preferably 50° C.-120° C., and more preferably 50° C.-100° C. The reaction time of the monocyclopentadienyl ligand with the Group 4 metal amino compound may be in the range of 6-168 hours, preferably 10-72 hours, and more preferably 12-48 hours. When the reaction temperature is less than 30° C., the ligand is insufficiently reacted with the metal amino compound and thus the yield and purity of the reaction product decrease. When the reaction temperature is higher than 150° C., the reaction product is thermally unstable and thus the yield and purity of the reaction product decreases. When the reaction time is shorter than 6 hours, the ligand is insufficiently reacted with the metal amino compound, whereas when the reaction time is longer than 168 hours, the obtained products may be changed into a different metal compound. In operation (d), the silane compound may be selected from chlorotrimethylsilane, dichlorodimethylsilane, trichloromethylsilane, and tetrachlorosilane. The mol ratio of the Group 4 metal compound that will react to the silane compound may be in the range of 1:1 to 1:5, and preferably 1:2 to 1:3. When the mol ratio of the Group 4 metal compound to the silane compound is less than 1:1, the chloride substitution occurs insufficiently and thus the yield and purity of the product decrease. On the other hand, when the mol ratio of the Group 4 metal compound to the silane compound is greater than 1:5, the obtained product can be changed into a different metal compound due to excess silane compound. In this case, however, excess silane compound may not affect significantly.

A method of preparing transition metal complexes of Formulae 1 through 3 according to another embodiment of the present invention includes: (a) synthesizing a compound of Formula 6 by reacting a boronic acid compound of Formula 8 with a 2-bromoaniline compound of Formula 9; (b) synthesizing a compound of Formula 7 by the compound of Formula 6 with R₁Li and then adding an acid thereto; (c) synthesizing a compound of Formula 4 by reacting a compound of Formula 7 with R₃X where X is a halogen atom; and (d) synthesizing a complex of Formula 1 or Formula 2 by reacting the comound of Formula 4 with the compound of Formula 10 and then adding (CH₃)_(n)SiX_(4-n) where X is a halogen atom and n is 0, 1, 2, or 3 thereto. The present method is the same as the previous method, except that operation b and operation c of the previous method correspond to operation c′ and operation b′ of the present method, respectively. Respective operations of the present method is the same as in the previous method.

Methods of synthesizing the complexe of Formula 1 may be represented by Reaction Scheme 1 or Reaction Scheme 2:

These Reaction Schemes can also be used to the complexes of Formula 2, and Formula 3.

Meanwhile, the complex of Formula 3 can be synthesized using other methods. For example, a method of synthesizing the complex of Formula 3 includes: e) synthesizing a dilithium form of the compound of Formula 7 by reacting a compound of Formula 7 with an alkyllihtium that is a base; and f) synthesizing a complex of Formula 3 by reacting an in-situ mixtures composed of the dilithium compound, alkyllithium and MX₄ where X is halogen and M is a transition metal of Group 4, which is represented by Reaction Scheme 3:

The Group 4 transition metal complex of Formula 3 can be easily synthesized using the method represented by Reaction Scheme 3, not using the Group 4 transition metal complex of Formula 10 and the silicon compound in operation (d) of the methods of synthesizing the complexes of Formula 1 through Formula 3. Accoridng to operation (e) of Reaction Scheme 3, in the prescence of THF or diethylether, the ligand of Formula 7 is reacted with 2 eq. n-BuLi that is a strong base, thereby forming a dilithiated solid compound. According to operation (f), at a low temperature of −78° C., a Group 4 metal tetrachloride is reacted with 2 eq. alkyllithium compound, such as MeLi, thereby forming Me₂MCl₂(solvent)_(n) where M is Ti or Zr, a solvent is THF or Et₂O, n is 1 or 2. And, the dilithium salt compound prepared in operation (e) reacts in-situ with the Me₂MCl₂(solvent)_(n) to obtain the complex of Formula 3. When this method is used, the complex of Formula 3, in particular, a complex of Formula 3 where Q₁ and Q₂ are directly substituted with alkyl or aryl group can be obtained with a large yield (70% or more).

A catalyst composition according to an embodiment of the present invention including: a complex of one of Formulae 1 through 3, and at least one cocatalyst selected from compounds of Formula 11 through 13. The catalyst composition can be used for homopolymerization or copolymerization of olefin: —[Al(R₇)—O]_(a)—  (11) where R₇ is each independently a halogen radical; a C1-C20 hydrocarbyl radical; or a C1-C20 hydrocarbyl radical substituted with halogen, a is an integer of 2 or greater; D(R₇)₃   (12) where D is aluminum or boron, R₇ is described above; and [L-H]⁺[Z(A)₄]⁻, or [L]⁺[Z(A)₄]⁻  (13) where L is a neutral or cationic Lewis acid, H is a hydrogen atom; Z is an element of Group 13; and A is each independently a C6-C20 aryl or alkyl radical in which at least one hydrogen atom is substituted with halogen or a C1-C20 hydrocarbyl, alkoxy, or penoxy radical.

A method of preparing the catalyst composition according to an embodiment of the present invention include contacting the transition metal complex with the compound of Formula 11 or Formula 12 to obtain a mixture, and adding a compound of Formula 13 to the mixture. A method of preparing the catalyst composition according to another embodiment of the present invention includes contacting the transition metal complex with the compound of Formula 11.

In the former method of preparing a catalyst composition, the mole ratio of the transition metal complex to the compound of Formula 11 or Formula 12 may be in the range of 1:2 to 1:5,000, preferably 1:10 to 1:1,000, and preferably 1:20 to 1:500, and the mole ratio of the transition metal complex to the compound of Formula 13 may be in the range of 1:1 to 1:25, preferably 1:1 to 1:10, and most preferably 1:2 to 1:5. When the mole ratio of the transition metal complex to the compound of Formula 1 1 or Formula 12 is less than 1:2, the amount of the alkylating agent is so small that the metal compound is insufficiently alkylated. On the other hand, the mole ratio of the transition metal complex to the compound of Formula 11 or Formula 12 is greater than 1:5,000, the metal compound is alkylated, but excess alkylating agent can react with the activator of Formula 13 so that the alkylated metal compound is less activated. When the mole ratio of the transition metal complex to the compound of Formula 13 is less than 1:1, the amount of the activator is relatively small so that the metal compound is less activated. On the other hand, when the ratio of the transition metal complex to the compound of Formula 13 is greater than 1:25, the metal compound may be completely activated but excess activator remains, that is, the preparation process for the catalyst composition is expensive, and the obtained polymer purity is poor.

In the latter method of preparing the catalyst composition, the mol ratio of the transition metal complex to the compound of Formula 11 may be in the range of 1:10 to 1:10,000, preferably 1:100 to 1:5,000, and most preferably 1:500 to 1:2,000. When the mole ratio of the transition metal complex to the compound of Formula 11 is less than 1:10, the amount of the compound of Formula 11 is relatively small so that the transition metal complex is less activated and the obtained catalyst composition has low activity. On the other hand, when the mole ratio of the transition metal complex to the compound of Formula 11 is greater than 1:10,000, the metal compound is completely activated but excess activator remains, that is, the preparation process for the catalyst composition is expensive, and the obtained polymer purity is poor.

The reaction solvent used to preparing the activated catalyst composition can be a hydrocarbon based solvent, such as pentane, hexane, and heptane, or an aromatic solvent, such as benzene and toluene. The transition metal complexes of Formulae 1 through 3 and the cocatalysts can be supported by silica or alumina for use.

Examples of the compound of Formula 11 may include methylaluminoxane, ethylaluminoxane, isobutylaluminoxane, butylaluminoxane etc. For example the compound of Formula 11 is methylaluminoxane.

Examples of the alkyl metal compound of Formula 12 may include trimethylaluminum, triethylaluminum, triisobutylaluminum, tripropylaluminum, tributylaluminum, dimethylchloroaluminum, triisopropylaluminum, tri-s-butylaluminum, tricyclopentylaluminum, tripentylaluminum, triisopentylaluminum, trihexylaluminum, trioctylaluminum, ethyldimethylaluminum, methyldiethylaluminum, triphenylaluminum, tri-p-tolylaluminum, dimethylaluminummethoxide, dimethylaluminmethoxide, trimethylboron, triethylboron, triisobutylboron, tripropylboron, tributylboron etc. For example, the alkyl metal compound of Formula 12 is trimethylaluminum, triethylaluminum, or triisobutylaluminum.

Examples of the compound of Formula 13 may include triethylammoniumtetraphenylboron, tributylammoniumtetraphenylboron, trimethylammoniumtetraphenylboron, tripropylammoniumtetraphenylboron, trimethylammoniumtetra(p-tolyl)boron, trimethylammoniumtetra(o,p-dimethylphenyl)boron, tributylammoniumtetra(p-trifluoromethylphenyl)boron, trimethylammoniumtetra(p-trifluoromethylphenyl)boron, tributylammoniumtetrapentafluorophenylboron, N,N-diethylanilinium tetraphenylboron, N,N-diethylaniliniumtetraphenylboron, N,N-diethylaniliniumtetrapentafluorophenylboron, diethylammoniumtetrapentafluorophenylboron, triphenylphosphoniumtetraphenylboron, trimethylphosphoniumtetraphenylboron, triethylammoniumtetraphenylaluminum, tributylammoniumtetraphenylaluminum, trimethylammoniumtetraphenylaluminum, tripropylammoniumtetraphenylaluminum, trimethylammoniumtetra(p-tolyl)aluminum, tripropylammoniumtetra(p-tolyl)aluminum, triethylammoniumtetra(o,p-dimethylphenyl)aluminum, tributylammoniumtetra(p-trifluoromethylphenyl)aluminum, trimethylammoniumtetra(p-trifluoromethylphenyl)aluminum, tributylammoniumtetrapentafluorophenylaluminum, N,N-diethylaniliniumtetraphenylaluminum, N,N-diethylaniliniumtetraphenylaluminum, N,N-diethylaniliniumtetrapentafluorophenylaluminum, diethylammoniumtetrapentatetraphenylaluminum, triphenylphosphoniumtetraphenylaluminum, trimethylphosphoniumtetraphenylaluminum, triethylammoniumtetraphenylaluminum, tributylammoniumtetraphenylaluminum, trimethylammoniumtetraphenylboron, tripropylammoniumtetraphenylboron, trimethylammoniumtetra(p-tolyl)boron,tripropylamoniumtetra(p-tolyl)boron, triethylammoniumtetra(o,p-dimethylphenyl)boron, trimethylammoniumtetra(o,p-dimethylphenyl)boron, tributylammoniumtetra(p-trifluoromethylphenyl)boron, trimethylammoniumtetra(p-trifluoromethylphenyl)boron, tributylammoniumtetrapentafluorophenylboron, N,N-diethylaniliniumtetraphenylboron, N,N-diethylaniliniumtetraphenylboron, N,N-diethylaniliniumtetrapentafluorophenylboron, diethylammoniumtetrapentafluorophenylboron, triphenylphosphoniumtetraphenylboron, triphenylcarboniumtetra(p-trifluoromethylphenyl)boron, triphenylcarboniumtetrapentafluorophenylboron etc.

A method of preparing a homopolymer or copolymer of polyolefin according to an embodiment of the present invention includes contacting a catalyst composition that contains the complex of one of Formulae 1 through 3 and at least one compound selected from compounds of Formulae 11 through 13 with at least one olefin monomer.

A polymerization process using the catalyst composition may be a solution process, but when the catalyst composition is used together with an inorganic support, such as silica, the polymerization process can also be a slurry or vapor process.

The catalyst composition can be melted or diluted in a solvent suitable for olefin polymerization, before being used. The solvent can be a C5-C12 aliphatic hydrocarbon solvent, such as pentane, hexane, heptane, nonane, decane, or isomers of these; an aromatic hydrocarbon, such as toluene or benzene; or a hydrocarbon solvent that is substituted with a chloride atom, such as dichloromethane or chlorobenzene. The solvent used therein may be treated with a small amount of alkylaluminum to remove water or air, which acts as a catalyst poison. When needed, more cocatalysts such as alkylaluminium can be used for the same purpose.

Examples of an olefin based monomer that can be polymerized using the metal complexes and the coatalysts may include ethylene, alpha-olefin, cyclic olefin etc. In addition, a diene or triene olefin-based monmer having at least two double bonds can be polymerized. In particular, the olefin-based monomer can be ethylene, propylene, 1-butene, 1-pentene, 4-methyl-1-pentene, 1-hexene, 1-heptene, 1-octene, 1-decene, 1-undecene, 1-dodecene, 1-tetradecene, 1-hexadecene, 1-itocene, norbornene, norbonadiene, ethyllidenenorbonene, phenylnorbonene, vinylnorbonene, dicyclopentadiene, 1,4-butadiene, 1,5-pentadiene, 1,6-hexadiene, stylene, alpha-methylstylene, divinylbenzene, or 3-chloromethylstylene. In addition, at least two different monomers of these can be copolymerized. The catalyst composition according to an embodiment of the present invention is used to copolymerze ethylene and 1-octene having large steric hindrance at a high reaction temperature of 90° C. to thereby obtain a copolymer having high molecular weight but having a very low density less than 0.910 g/cc.

A monomer of the copolymer may include ethylene and at least one compound selected from propylene, 1-butene, 1-hexene, and 4-methyl-1-pentene, and 1-octene.

The present invention will be described in further detail with reference to the following examples. These examples are for illustrative purposes only and are not intended to limit the scope of the present invention.

Synthesis of Ligand and Metal Complex

Organic reagents and solvents were obtained from Aldrich Co., Inc. and Merck Co., Inc. and purified using a standard method. Each process for the synthesis was performed being isolated from air and moisture to improve reproducibility of experiments. The structure of compounds was identified using a 400 MHz nuclear magnetic resonance (NMR) and an X-ray spectrometer.

EXAMPLE 1 2-dihydroxyboryl-3-methyl-2-cyclopenten-1-one

44.80 g (204.49 mmol) of 2-bromo-3-methyl-2-cyclopenten-1-on ethylene ketal compound were mixed with 240 mL of THF, and then 82 mL(204.49 mmol) of n-BuLi (2.5M in hexane) was added thereto at −78° C. The resultant mixture was mixed at −78° C. for one hour. Then, 42.31 g (224.95 mmol) of boron triisopropylester was added to the reaction product and then mixed at −60° C. or less for one hour. The resultant mixture was further reacted at −50° C. for 30 minutes, and then 110 mL of 2 N HCl was added thereto and mixed for 10 minutes. Subsequently, the reaction product was loaded to a separating funnel, 200 mL of ethylacetate (E.A) was added thereto, and then an organic layer was extracted therefrom. 55 mL of ethyl acetate (E.A) was used twice to extract the organic layer. The collected organic layer was dried over MgSO₄ to remove water therein and filtered using a glass filter. The solvent contained in the dried product was removed using a rotary vacuum evaporator to obtain a solid product. The solid product was melted using 300 mL of E.A and then twice recrystallized at −30° C. The remaining organic layer was column chromatographed (hexane:E.A=1:1) to remove by-products, and then recrystallized (24.30 g, 85%)

¹H NMR (CDCl₃): =6.75(s, 2H, OH), 2.69-2.67(m, 2H, CH₂), 2.51-2.49(m, 2H, CH₂), 2.45(s, 3H, CH₃); ¹³C {¹H} NMR (CDCl₃): =217.35, 193.42, 35.73, 35.12, 20.42

EXAMPLE 2 2-dihydroxyboryl-3,4-dimethyl-2-cyclopenten-1-one

2-dihydroxyboryl-3,4-dimethyl-2-cyclopenten-1-one was obtained in the same manner as in Example 1 using 2-bromo-3,4-dimethyl-2-cyclopenten-1-one ethylene ketal compound (86%).

¹H NMR (CDCl₃): δ 1.24 (d, J=3.6 Hz, 3H, CH₃), 2.09 (dd, J=19, 2.0 Hz, 1H, CH₂), 2.39 (s, 3H, CH₃), 2.72 (dd, J=19, 6.8 Hz, 1H, CH₂), 2.84-2.86 (m, 1H, CH), 7.29 (s, 2H, OH) ppm. ¹³C{¹H} NMR(CDCl₃): δ 18.01, 18.90, 40.76, 44.22, 197.08, 216.12 ppm.

EXAMPLE 3 2-(2-aminophenyl)-3-methyl-2-cyclopenten-1-one

4.00 g (28.584 mmol) of 2-dihydroxyboryl-3-methyl-2-cyclopenten-1-one compound, 0.30 g (0.260 mmol) of tetrakis(triphenylphosphine)palladium, 4.13 g (38.978 mmol) of sodium carbonate were loaded to 250 mL schlenk flask, and then 80 mL of degassing DME and 27 mL of H₂O that had been purged with N₂ were added thereto using a syringe. 4.47 g (25.985 mmol) of 2-bromoaniline was added to the flask using a syringe and reacted at 90° C. for 12 hours.

Subsequently, the reaction product, 200 mL of ethylacetate, and 100 mL of H₂O were added to a separating funnel. Then, the organic layer was extracted. Subsequently, 100 mL of ethylacetate was added to the aqueous liquid to extract an organic layer again. The organic layer was dried over MgSO₄ to remove water therein and then a rotary vacuum evaporator was used to remove the remaining solvent. Then, the resultant organic layer was column chromatographed (hexane:E.A=1:1) (3.55 g, 73%).

¹H NMR (CDCl₃): =7.12 (td, J=7.6 Hz, 1H, Ph), 6.89 (dd, J=7.6 Hz, 1H, Ph), 6.77 (td, J=7.6 Hz, 1H, Ph), 6.72 (dd, J=7.6 Hz, 1H, Ph), 3.72 (br s, 2H, NH₂), 2.71-2.68 (m, 2H, CH₂ ^(Cp)), 2.56-2.54 (m, 2H, CH₂ ^(Cp)), 2.08 (s, 3H, CH₃); ¹³C {¹H} NMR (CDCl₃): =207.84, 174.84, 144.60, 139.42, 130.44, 128.73, 118.13, 117.84, 116.30, 34.74, 32.13, 18.56

EXAMPLE 4 2-(2-amino-4-fluorophenyl)-3-methyl-2-cyclopenten-1-one

4.937 g (25.982 mmol) of 2-bromo-4-fluoroaniline, 4.00 g (28.584 mmol) of 5-methyl-1-cyclopenten-2-one boronic acid compound, 0.30 g (0.260 mmol) of tetrakis(triphenylphosphine)palladium, and 4.13 g (38.978 mmol) of sodium carbonate were loaded to 250 mL schlenk flask, and then 80 mL of degassing DME and 27 mL of H₂O that had been purged with N₂ were added thereto using a syringe. The mixture was reacted at 90° C. for 12 hours. The work-up was the same as in Example 3 (3.84 g, 72%).

¹H NMR (CDCl₃): =6.83 (t, J=7.6 Hz, 1H, Ph), 6.48 (t, J=7.6 Hz, 1H, Ph), 6.43 (d, J=10.4 Hz, 1H, Ph), 3.82 (br s, 2H, NH₂), 2.73-2.71 (m, 2H, CH₂ ^(Cp)), 2.58-2.55 (m, 2H, CH₂ ^(Cp)), 2.09 (s, 3H, CH₃); ¹³C {¹H} NMR (CDCl₃): =207.93, 175.26, 168.18(d, J=242.6 Hz, PhC—F) 146.47(d, J=5.7 Hz, Ph), 138.76, 131.90(d, J=9.8 Hz, Ph), 113.71, 105.08(d, 22 Hz, Ph), 102.91(d, 22 Hz, Ph), 34.79, 32.22, 18.63

EXAMPLE 5 2-(2-amino-5-fluorophenyl)-3-methyl-2-cyclopenten-1-one

4.46 g (21.44 mmol) of 2-bromo-4-fluoroaniline, 3.30 g (23.582 mmol) of 5-methyl-1-cyclopenten-2-one boronic acid compound, 0.204 g (0.177 mmol) of tetrakis(triphenylphosphine)palladium, and 3.41 g (32.173 mmol) of sodium carbonate were loaded to 250 mL schlenk flask, and then 66 mL of degassing DME and 22 mL of H₂O that had been purged with N₂ were added thereto using a syringe. The mixture was reacted at 90° C. for 12 hours. The work-up was the same as in Example 3 (3.76 g, 79%).

¹H NMR (CDCl₃): =6.74(td, J=8.8 Hz, 1H, Ph), 6.45(d, J=7.6 Hz, 1H, Ph), 3.65 (br s, 2H, NH₂), 2.71-2.69(m, 2H, CH₂ ^(Cp)), 2.54-2.52(m, 2H, CH₂ ^(Cp)), 2.07(s, 3H, CH₃); ¹³C {¹H} NMR (CDCl₃): =207.05, 176.05, 155.17(d, J=12.9 Hz, Ph), 152.63(dd, J=12.9 Hz, Ph), 150.11(d, J=12.9 Hz, Ph), 137.79, 129.60(d, J=3.1 Hz, Ph), 120.43(dd, J=12.9 Hz, Ph), 111.97(dd, 1.8 Hz, 22 Hz, Ph), 103.00(t, 22 Hz, Ph), 34.66, 32.28, 18.50

EXAMPLE 6 2-(2-amino-5-methylphenyl)-3-methyl-2-cyclopenten-1-one

1.607 g (8.031 mmol) of 2-bromo-4-methylaniline, 1.180 g (8.432 mmol) of 5-methyl-1-cyclopenten-2-one boronic acid compound, 0.093 g (0.080 mmol) of tetrakis(triphenylphosphine)palladium, and 1.277 g (12.047 mmol) of sodium carbonate were were loaded to 250 mL schlenk flask, and then 24 mL of degassing DME and 8 mL of H₂O that had been purged with N₂ were added thereto using a syringe. The mixture was reacted at 90° C. for 12 hours. The work-up was the same as in Example 3 (1.66 g, 96%).

¹H NMR (CDCl₃): =6.88(s, 1H, Ph), 6.60(s, 1H, Ph), 3.49(br s, 2H, NH₂), 2.74?? 2.72(m, 2H, CH₂ ^(Cp)), 2.60??2.58(m, 2H, CH₂ ^(Cp)), 2.24(s, 3H, CH₃), 2.19(s, 3H, CH₃), 2.10(s, 3H, CH₃); ¹³C {¹H} NMR (CDCl₃): =207.97, 174.68, 140.18, 139.97, 131.04, 128.58, 126.96, 123.00, 117.56, 34.93, 32.19, 20.48, 18.71, 17.89

EXAMPLE 7 2-(2-(2-mesitylenesulfonyl)aminophenyl)-3-methyl-2-cyclopenten-1-one

0.500 g (2.67 mmol) of 2-(2-aminophenyl)-3-methyl-2-cyclopenten-1-one, 0.253 g (3.204 mmol) of pyridine, 0.584 g (2.67 mmol) of 2-mesitylenesulfonyl chloride), and 2 mL of M.C (methylene chloride) were loaded to a 20 mL vial, and then reacted for 12 hours. 10 mL of M.C and 4 mL of 2 N HCl were added to the reaction product. The resultant organic layer is collected and then dried over MgSO₄ to remove water. The solvent contained in the dried product was removed using a rotary vacuum evaporator. The obtained solid was washed with 10 mL of diethyl ether and filtered using a glass filter. The filtered product was dried in vacuum to remove the solvent that had remained therein (0.790 g, 80%).

¹H NMR (CDCl₃): =7.51(d, J=7.6 Hz, 1H, Ph), 7.22(t, J=7.6 Hz, 1H, Ph), 7.07 (t, J=7.6 Hz, 1H, Ph), 6.96(d, J=7.6 Hz, 1H, Ph), 6.83(s, 2H, Ph^(Mes)), 6.77(s, 1H, NH), 2.44-2.40(m, 4H, CH₂*2), 2.42(s, 6H, Ph^(Mes)), 2.36(s, 3H, Ph^(Mes)), 1.76(s, 3H, CH₃).

EXAMPLE 8 2-(2-(2-mesitylenesulfonyl)amino-4-fluorophenyl)-3-methyl-2-cyclopenten-1-one

0.800 g (3.90 mmol) of 2-(2-amino-4-fluorophenyl)-3-methyl-2-cyclopenten-1-one, 0.339 g (4.29 mmol) of pyridine, 0.938 g (4.29 mmol) of 2-mesitylenesulfonyl chloride, and 4 mL of M.C were loaded to a 20 mL vial, and then reacted for 12 hours. The work-up was the same as in Example 7 (1.29 g, 85%).

¹H NMR (CDCl₃): =7.84(s, 1H, NH), 7.19(d, J=6.0 Hz, 1H, Ph), 6.90(m, 2H, Ph), 6.84(s, 2H, Ph^(Mes)), 2.54-2.46(m, 4H, CH₂ ^(Cp)*2), 2.09(s, 3H, CH₃), 2.39(s, 6H, Ph^(Mes)), 2.28(s, 3H, Ph^(Mes)), 1.80(s, 3H, CH₃); ¹³C {¹H} NMR (CDCl₃): =208.89, 177.35, 163.41. 160.93, 141.81, 139.72, 138.26, 136.26, 134.87, 131.79, 131.72, 123.23, 114.95, 113.20, 34.63, 32.81, 23.31, 20.92, 18.57

EXAMPLE 9 2-(2-(2-mesitylenesulfonyl)amino-5-fluorophenyl)-3-methyl-2-cyclopenten-1-one

0.700 g (3.14 mmol) of 2-(2-amino-5-fluorophenyl)-3-methyl-2-cyclopenten-1-one, 0.273 g (3.45 mmol) of pyridine, 0.754 g (3.45 mmol) of 2-mesitylenesulfonyl chloride, and 3 mL of M.C were loaded to a 20 mL vial, and then reacted for 12 hours. The work-up was the same as in Example 7 (0.760 g, 60%).

¹H NMR (CDCl₃): =7.05(s, 1H, NH), 6.90(s, 1H, Ph), 6.87(s, 2H, Ph^(Mes)), 6.54(d, J=7.6 Hz, 1H, Ph), 2.54-2.46(m, 4H, CH₂ ^(Cp)*2), 2.42(s, 6H, CH₃Ph^(Mes)), 2.31(s, 3H, CH₃), 2.01(s, 3H, CH₃); ¹³C {¹H} NMR (CDCl₃): =207.55, 177.49, 162.06, 159.63, 159.10, 141.71, 138.76, 137.87, 135.55, 133.99, 131.67, 112.72, 104.67, 34.70, 32.84, 23.40, 21.02, 18.83

EXAMPLE 10 2-(2-(2-mesitylenesulfonyl)amino-5-methylphenyl)-3-methyl-2-cyclopenten-1-one

0.700 g (3.25 mmol) of 2-(2-amino-5-methylphenyl)-3-methyl-2-cyclopenten-1-one, 0.283 g (3.58 mmol) of pyridine, 0.782 g (3.58 mmol) of 2-mesitylenesulfonyl chloride, and 3 mL of M.C were loaded to a 20 mL vial, and then reacted for 12 hours. The work-up was the same as in Example 7 (1.29 g, 85%).

¹H NMR (CDCl₃): =7.24(s, 1H, NH), 7.01(s, 1H, Ph), 6.76(s, 2H, Ph^(Mes)), 6.48(s, 1H, Ph), 2.43-2.39 (m, 4H, CH₂ ^(Cp)*2), 2.41 (s, 3H, CH₃), 2.36(s, 6H, Ph^(Mes)), 2.25(s, 6H, PhCH₃*2), 1.92(s, 3H, Ph^(Mes)); ¹³C {¹H} NMR (CDCl₃): =207.97, 174.68, 140.18, 139.97, 132.24, 131.58, 131.04, 130.15, 129.57, 128.58, 126.96, 123.00, 117.56, 34.93, 32.19, 23.09 20.48, 19.89, 18.71, 17.89

EXAMPLE 11 2-(2-(p-toluenesulfonyl)aminophenyl)-3-methyl-2-cyclopenten-1-one

0.815 g (4.35 mmol) of 2-(2-aminophenyl)-3-methyl-2-cyclopenten-1-one, pyridine 0.413 g (5.22 mmol), 0.829 g (5.22 mmol) of p-toluenesulfonyl chloride, and 4 mL of M.C were loaded to a 20 mL vial, and then reacted for 12 hours. The work-up was the same as in Example 7 (1.330 g, 89%).

¹H NMR (CDCl₃): =7.80(s, 1H, NH), 7.55(d, 1H, Ph), 7.43(d, J=8.0 Hz, 2H, Ph^(Ts)), 7.33(t, 1H, Ph), 7.19(t, 1H, Ph), 7.12(d, J=8.0 Hz, 2H, Ph^(Ts)), 6.89(d, 1H, Ph), 2.43-2.40(m, 4H, CH₂ ^(Cp)*2), 2.36(s, 3H, CH₃), 1.75(s, 3H, CH₃); ¹³C {¹H} NMR (CDCl₃): =208.91, 177.40, 142.75, 138.71, 137.33, 134.29, 130.62, 129.09, 129.00, 127.78, 127.04, 126.52, 126.13, 34.52, 32.61, 21.42, 18.76

EXAMPLE 12 2-(2-(p-toluenesulfonyl)amino-5-fluorophenyl)-3-methyl-2-cyclopenten-1-one

0.700 g (3.14 mmol) of 2-(2-amino-5-fluorophenyl)-3-methyl-2-cyclopenten-1-one, 0.298 g (3.76 mmol) of pyridine, 0.598 g (3.76 mmol) of p-toluenesulfonyl chloride, and 3 mL of M.C were loaded to a 20 mL vial, and then reacted for 12 hours. The work-up was the same as in Example 7 (1.000 g, 85%).

¹H NMR (CDCl₃): =7.62(s, 1H, NH), 7.52(s, 1H, Ph), 7.38(d, J=8.0 Hz, 2H, Ph^(Ts)), 7.28(s, 1H, Ph), 7.06(d, J=8.0 Hz, 2H, Ph^(Ts)), 2.39-2.35(m, 4H, CH₂ ^(Cp)*2), 2.25(s, 3H, CH₃), 1.69(s, 3H, CH₃); ¹³C {¹H} NMR (CDCl₃): =207.56, 175.29, 141.94, 138.54, 136.27, 134.38, 130.62, 128.95, 128.57, 127.57, 126.96, 126.43, 125.93, 34.54, 33.08, 22.06, 17.91

EXAMPLE 13 2-(2-(p-toluenesulfonyl)amino-5-methylphenyl)-3-methyl-2-cyclopenten-1-one

0.600 g (2.79 mmol) of 2-(2-amino-5-methylphenyl)-3-methyl-2-cyclopenten-1-one, 0.243 g (3.07 mmol) f pyridine, 0.858 g (3.07 mmol) of p-toluenesulfonyl chloride, and 3 mL of M.C were loaded to a 20 mL vial, and then reacted for 12 hours. The work-up was the same as in Example 7 (0.800 g, 78%).

¹H NMR (CDCl₃): =7.28(s, 1H, NH), 7.21(d, J=8.0 Hz, 2H, Ph^(Ts)), 7.14(s, 1H, Ph), 6.76(d, J=8.0 Hz, 2H, Ph^(Ts)), 6.86(s, 1H, Ph), 2.43-2.39 (m, 4H, CH₂ ^(Cp)*2), 2.41 (s, 3H, CH₃), 2.25(s, 6H, PhCH₃*2), 1.92(s, 3H, Ph^(Ts)); ¹³C {¹H} NMR (CDCl₃): =208.95, 172.54, 139.54, 139.95, 132.24, 131.58, 130.84, 130.55, 129.52, 129.47, 128.96, 122.84, 116.52, 34.85, 31.94, 22.86 20.25, 19.67, 17.57

EXAMPLE 14 2-(2-amino)phenyl-3,4-dimethyl-2-cyclopenten-1-one

Yellow oil was obtained in the same manner as in Example 3, using 4.000 g (25.984 mmol) of 2-dihydroxyboryl-3,4-dimethyl-2-cyclopenten-1-one, 3.443 g (32.497 mmol) of sodium carbonate, 0.751 g (0.650 mmol) of tetrakis(triphenylphosphine)palladium, and 3.725 g (21.653 mmol) of 2-bromoaniline (2.872 g, 66%).

¹H NMR (CDCl₃): δ 1.32(d, J=3.6 Hz, 3H, CH₃), 2.07(s, 3H, CH₃), 2.19(dd, J=18.4, 1.6 Hz, 1H, CH₂—H), 2.83(dd, J=18.4, 6.4 Hz, 1H, CH₂—H), 2.86(qd, J=6.4, 1.6 Hz, 1H, CH—H), 3.72(br s, 2H, NH₂), 6.77(dd, J=7.6, 1.6 Hz, 1H, Ph), 6.81(td, J=7.6, 1.6 Hz, 1H, Ph), 6.91(dd, J=7.6, 1.6 Hz, 1H, Ph), 7.15(td, J=7.6, 1.6 Hz, 1H, Ph) ppm. ¹³C{¹H} NMR(CDCl₃): δ 16.39, 19.39, 37.97, 43.51, 116.60, 117.01, 118.16, 118.55, 128.97, 130.67, 144.45, 178.93, 207.02 ppm.

EXAMPLE 15 2-(2-amino-3,5-dimethyl)phenyl-3,4-dimethyl-2-cyclopenten-1-one

White solid was obtained in the same manner as in Example 3, using 3.459 g (22.465 mmol) of 2-dihydroxyboryl-3,4-dimethyl-2-cyclopenten-1-one, 2.976 g (28.076 mmol) of sodium carbonate, 0.649 g (0.562 mmol) of tetrakis(triphenylphosphine)palladium, and 3.745 g (18.718 mmol) of 2-bromo-4,6-dimethylaniline (3.161 g, 74%).

¹H NMR (CDCl₃): δ 1.32(d, J=3.6 Hz, 3H, CH₃), 2.04(s, 3H, CH₃), 2.18(s, 3H, CH₃), 2.20(s, 1H, CH₂—H), 2.24(s, 3H, CH₃), 2.82(dd, J=18.4, 6.4 Hz, 1H, CH₂—H), 2.94(qd, J=6.4, 1.6 Hz, 1H, CH—H), 3.48(br s, 2H, NH₂), 6.60(s, 1H, Ph), 6.88(s, 1H, Ph) ppm. ¹³C{¹H} NMR(CDCl₃): δ 16.19, 17.76, 19.32, 20.37, 37.67, 43.45, 117.42, 122.79, 126.74, 128.44, 130.88, 140.02, 178.58, 106.85 ppm.

EXAMPLE 16 2-(2-amino-3,5-difluoro)phenyl-3,4-dimethyl-2-cyclopenten-1-one

White solid was obtained in the same manner as in Example 3, using 2.000 g (12.990 mmol) of 2-dihydroxyboryl-3,4-dimethyl-2-cyclopenten-1-one, 1.967 g (18.557 mmol) of sodium carbonate, 0.429 g (0.371 mmol) of tetrakis(triphenylphosphine)palladium, and 2.436 g (12.371 mmol) of 2-bromo-4,6-difluoroaniline (1.938 g, 76%).

¹H NMR (CDCl₃): δ 1.29(d, J=3.6 Hz, 3H, CH₃), 2.04(s, 3H, CH₃), 2.15(dd, J=18.8, 2.0 Hz, 1H, CH₂—H), 2.79(dd, J=18.8, 14.4 Hz, 1H, CH₂—H), 2.93(q, J=6.4 Hz, 1H, CH—H), 3.65(br s, 2H, NH₂), 6.54(d, J_(H—F)=8.8 Hz, 1H, Ph), 6.78(t, J_(H—F)=8.8 Hz, 1H, Ph) ppm.

EXAMPLE 17 2-(2,5-dimethylcyclopenta-1,4-dienyl)phenyl(2-mesitylenesulfonyl)amine

0.645 g (1.746 mmol) of 2-(2-(2-mesitylenesulfonyl)aminophenyl)-3-methyl-2-cyclopenten-1-one and 12 mL of THF were loaded to a 50 mL flask, and then 2.30 mL (3.677 mmol) of MeLi (1.6 M in diethyl ether) was added thereto at −78° C. and stirred at the same temperature for two hours. The reaction product was stirred for 2 hours while the temperature was slowly raised. 10 mL of distilled water was added to the resultant reaction product and the THF contained therein was removed using a rotary vacuum evaporator. 10 mL of E.A and 5 mL of 2 N HCl were added to the reaction product from which the THF had been removed and strongly stirred for 3 minutes. Subsequently, the organic layer was collected from the stirred reaction product. 5 mL of E.A was twice added to the aqueous layer to obtain the organic layer. The collected organic layer was neutralized using 5 mL of NaHCO₃ and dried over MgSO₄ to remove water contained therein. The solvent contained in the dried produt was removed using a rotary vacuum evaporator. The product was filtered using a column chromatography (hexane: E.A=10:1) (0.550 g, 88%).

¹H NMR (CDCl₃): =7.51(d, J=7.6 Hz, 1H, Ph), 7.22 (t, J=7.6 Hz, 1H, Ph), 7.07 (t, J=7.6 Hz, 1H, Ph), 6.96 (d, J=7.6 Hz, 1H, Ph), 6.83(s, 2H, Ph^(Mes)), 6.77(s, 1H, NH), 2.44(m, 4H, CH₂*2), 2.46(s, 6H, Ph^(Mes)), 2.46(s, 3H, Ph^(Mes)), 1.76(s, 3H, CH₃)

EXAMPLE 18 2-(2,5-dimethylcyclopenta-1,4-dienyl)-4-fluorophenyl(2-mesitylenesulfonyl)amine

0.636 g (1.581 mmol) of CeCl₃ and 15 mL of THF were loaded to a 50 mL flask, and then 2.30 mL (3.677 mmol) of MeLi (1.6 M in diethyl ether) was added thereto at −78° C. 30 miutes after the resultant mixture turned yellow, 0.500 g (1.290 mmol) of 2-(2-(2-mesitylenesulfonyl)amino-4-fluorophenyl)-3-methyl-2-cyclopenten-1-one melted in 15 mL of THF was added to the flask using a syringe and stirred at −78° C. for 2 hours. The stirred product was stirred for one hour while the temperature was slowly raised. 8 mL of distilled water was added to the flask and the THF contained in the reaction product was removed using a rotary vacuum evaporator. 8 mL of E.A and 4 mL of 2 N HCl were added to the reaction product from which the THF had been removed, and then strongly stirred for 3 minutes. Subsequently, the organic layer was collected from the stirred reaction procut. 4 mL of E.A was twice added to the aqueous liquid to obtain the organic layer. The collected organic layer was neutralized using 4 mL of NaHCO₃ and dried over MgSO₄ to remove water contained therein. CeCl₃ and MgSO₄ were removed using a glass filter and the solvent contained in the dried product was removed using a rotary vacuum evaporator. The product was filtered using a column chromatography (hexane:E.A=10:1) (0.360 g, 72%).

EXAMPLE 19 2-(2,5-dimethylcyclopenta-1,4-dienyl)-5-fluorophenyl(2-mesitylenesulfonyl)amine

0.500 g (1.233 mmol) of 2-(2-(2-mesitylenesulfonyl)amino-5-fluorophenyl)-3-methyl-2-cyclopenten-1-one and 10 mL of THF were added to a 50 mL flask, and then 1.927 ml (3.083 mmol) of MeLi (1.6 M in diethyl ether) was added thereto at −78° C. and stirred at the same temperature for 2 hours. The reaction product was stirred for 2 hours while the temperature was slowly raised. The work-up was the same as in Example 17 (0.173 g, 35%).

¹H NMR (CDCl₃): =6.88(s, 2H, Ph^(Mes)), 6.84-6.81(m, 1H, Ph), 6.64-6.61(m, 1H, Ph), 6.09(s, 1H, NH), 5.89(s, 1H, CH₂ ^(Cp)), 2.85-2.84(m, 2H, CH₂ ^(Cp)), 2.50(s, 6H,CH₃*2), 2.31(s, 3H,CH₃), 1.82(s, 3H,CH₃), 1.68(s, 3H,CH₃); ¹³C {¹H} NMR (CDCl₃): =142.94, 142.19, 141.97, 141.69, 138.84, 131.53, 125.36, 125.05, 112.78, 112.57, 103.70, 103.45, 103.20, 94.58, 44.53, 22.96, 21.02, 14.77, 14.77, 14.49

EXAMPLE 20 2-(2,5-dimethylcyclopenta-1,4-dienyl)-5-methylphenyl(2-mesitylenesulfonyl)amine

0.500 g (1.258 mmol) of 2-(2-(2-mesitylenesulfonyl)amino-5-methylphenyl)-3-methyl-2-cyclopenten-1-one and 10 mL of THF were added to a 50 mL flask at −78° C., and 1.965 ml (3.145 mmol) of MeLi (1.6 M in diethyl ether) was added thereto. The following experiment was the same as in Exapmle 17 (0.182 g, 37%).

¹H NMR (CDCl₃): =7.03(s, 1H, Ph), 6.80(s, 2H, Ph^(Mes)), 6.65(s, 1H, Ph), 6.13(s, 1H, NH), 5.77(s, 1H, CH₂ ^(Cp)), 2.79-2.60(m, 2H, CH₂ ^(cp)), 2.43(s, 3H, CH₃), 2.36(s, 6H, CH₃ ^(mes)), 2.31(s, 3H, CH₃), 2.29(s, 3H, CH₃), 1.70(s, 3H, CH₃), 1.50(s, 3H, CH₃); ¹³C {¹H} NMR (CDCl₃): =142.41, 141.45, 140.08, 139.69, 138.78, 137.40, 136.41, 134.38, 131.51, 131.36, 130.98, 128.76, 128.45, 124.71, 44.14, 23.43, 23.09, 21.05, 20.96, 19.89, 14.71, 14.54

EXAMPLE 21 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)phenylamine

Brown solid was obtained in the same manner as in Example 18 using 9.598 g (38.973 mmol) of anhydrous CeCl₃, 24.358 mL (38.973 mmol) of MeLi (1.6 M in diethyl ether), and 2.615 g (12.991 mmol) of 2-(2-amino)phenyl-3,4-dimethyl-2-cyclopenten-1-one (2.307 g, 89%).

¹H NMR (CDCl₃): δ 1.56(s, 3H, Cp-CH₃), 1.75(s, 3H, Cp-CH₃), 1.85(s, 3H, Cp-CH₃), 2.82(s, 2H, Cp-CH₂), 3.55(br s, 2H, NH₂), 6.62(dd, J=7.6, 1.6 Hz, 1H, Ph), 6.65(td, J=7.6, 1.6 Hz, 1H, Ph), 6.82(dd, J=7.6, 1.6 Hz, 1H, Ph), 6.99(td, J=7.6, 1.6 Hz, 1H, Ph) ppm. ¹³C{¹H} NMR(CDCl₃): δ 11.67, 13.63, 14.35, 48.80, 114.67, 117.76, 122.79, 127.69, 130.13, 133.14, 135.54, 136.73, 139.61, 144.14 ppm.

EXAMPLE 22 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)-4,6-dimethylphenylamine

Yellow solid was obtained in the same manner as in Example 18 using 9.666 g (39.246 mmol) of anhydrous CeCl₃, 24.529 mL (39.246 mmol) of MeLi (1.6 M in diethyl ether), and 3.000 g (13.082 mmol) of 2-(2-amino-3,5-dimethyl)phenyl-3,4-dimethyl-2-cyclopenten-1-one (2.241 g, 75%).

¹H NMR (CDCl₃): δ 1.74(s, 3H, Cp-CH₃), 1.93(s, 3H, Cp-CH₃), 2.04(s, 3H, Cp-CH₃), 2.26(s, 3H, Ph—CH₃), 2.33(s, 3H, Ph—CH₃), 3.00(q, J=2.4 Hz, 2H, Cp-CH₂), 3.47(br s, 2H, NH₂), 6.72(s, 1H, Ph), 6.91(s, 1H, Ph) ppm. ¹³C{¹H} NMR(CDCl₃): δ 11.72, 13.61, 14.40, 17.88, 20.55, 48.78, 121.78, 122.61, 126.21, 128.20, 129.60, 133.00, 135.66, 136.41, 139.85, 140.07 ppm.

EXAMPLE 23 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)-4,6-fluorophenylamine

Yellow oil was obtained in the same manner as in Example 18 using (4.120 g, 16.730 mmol) of anhydrous CeCl₃, 29.206 mL (16.730 mmol) of MeLi (1.6 M in diethyl ether), and 1.300 g of (5.577 mmol) 2-(2-amino-3,5-difluoro)phenyl-3,4-dimethyl-2-cyclopenten-1-one (0.902 g, 70 %).

¹H NMR (CDCl₃): δ 1.67(s, 3H, Cp-CH₃), 1.87(s, 3H, Cp-CH₃), 1.97(s, 3H, Cp-CH₃), 3.96(br s, 2H, Cp-CH₂), 3.53(br s, 2H, NH₂), 6.52(d, J_(H—F)=8.8 Hz, 1H, Ph), 6.76(t, J_(H—F)=8.8 Hz, 1H, Ph) ppm. ¹³C{¹H} NMR(CDCl₃): δ 11.58, 13.60, 14.35, 48.95, 102.08, 111.67, 125.30, 128.98, 133.85, 134.76, 137.83, 137.96, 149.46, 151.96, 152.84, 155.19 ppm.

EXAMPLE 24 phenylene(2-mesitylenesulfonylamido)(2,5-dimethylcyclopentadienyl)titanium bis(dimethylamide)

0.200 g (0.544 mmol) of 2-(2,5-dimethylcyclopenta-1,4-dienyl)phenyl(2-mesitylene-sulfonyl)amine melted in 4 mL of toluene and 0.122 g (0.544 mmol) of Ti(NMe₂)₄diluted in 3 mL of toluene were loaded to a 25 mL flask, and then reacted at 50° C. for 12 hours. Toluene and dimethylamine contained in the raction product was removed in vacuum. The resulant product was solidated using pentane.

¹H NMR (CDCl₃): =7.19(d, J=7.6 Hz, 1H, Ph), 7.08(t, J=7.6 Hz, 1H, Ph), 6.98 (t, J=7.6 Hz, 1H, Ph), 6.91(d, J=7.6 Hz, 1H, Ph), 6.58(s, 2H, Ph^(Mes)), 5.69(s, 1H, CH₂ ^(Cp)), 3.24(s, 12H, N—CH₃), 2.64(s, 6H, CH₃*2), 2.08(s, 3H,CH₃) 1.74(s, 6H, CH₃*2)

EXAMPLE 25 5-fluorophenylene(2-mesitylenesulfonylamido)(2,5-dimethylcyclopenta-dienyl)titanium bis(dimethylamide)

The same experiment as in Example 24 was carried out, using 0.160 g (0.415 mmol) of 2-(2,5-dimethylcyclopenta-1,4-dienyl)-5-fluorophenyl(2-mesitylenesulfonyl)amine and 0.093 g (0.415 mmol) of Ti(NMe₂)₄.

¹H NMR (C₆D₆): =7.12(d, J=8.0 Hz, 1H, Ph), 6.71(t, J=8.0 Hz, 1H, Ph), 6.57(s, 2H, Ph^(Mes)), 6.46(td, J=8.0 Hz, 1H, Ph), 5.70(s, 2H, CH₂ ^(Cp)), 3.27(s, 12H, N—CH₃), 2.67(s, 6H,CH₃*2), 1.87(s, 3H,CH₃) 1.76(s, 6H, CH₃*2)

EXAMPLE 26 4-fluorophenylene(2-mesitylenesulfonylamido)(2,5-dimethylcyclopenta-dienyl)titanium bis(dimethylamide)

The same experiment as in Example 24 was carried out, using 0.158 g (0.392 mmol) of 2-(2,5-dimethylcyclopenta-1,4-dienyl)-4-fluorophenyl(2-mesitylenesulfonyl)amine and 0.093 g (0.415 mmol) of Ti(NMe₂)₄.

¹H NMR (C₆D₆): =6.69(s, 2H, Ph^(Mes)), 6.66-6.63(m, 1H, Ph), 6.52-6.47(m, 1H, Ph), 5.76(s, 2H, CH₂ ^(Cp)), 3.15(s, 12H, N—CH₃), 2.92(s, 6H, CH₃*2), 1.96(s, 6H,CH₃*2), 1.95(s, 3H, CH₃); ¹³C {¹H} NMR (C₆D₆): =140.50, 137.94, 131.63, 123.78, 112.60, 112.57, 112.39, 112.35, 112.21, 104.65, 104.41, 104.15, 51.36, 23.33, 23.30, 20.85, 13.88

EXAMPLE 27 4-methylphenylene(2-mesitylenesulfonylamido)(2,5-dimethylcyclopenta-dienyl)titanium bis(dimethylamide)

0.172 g (0.435 mmol) of 2-(2,5-dimethylcyclopenta-1,4-dienyl)-4-methylphenyl(2-mesitylenesulfonyl)amine and 0.093 g (0.415 mmol) of Ti(NMe₂)₄ were reacted at 80° C. Toluene and dimethylamine was removed from the reaction product in vacuum. The resultant reaction product was solidated using pentane.

EXAMPLE 28 2-(2,5-dimethylcyclopenta-1,4-dienyl)phenyl(p-toluenesulfonyl)amine

The same experiment as in Example 17 was carried out, using 1.000 g (2.93 mmol) of 2-(2-(p-toluenesulfonyl)aminophenyl)-3-methyl-2-cyclopenten-1-one and 3.660 ml (5.860 mmol) of MeLi (1.6 M in diethyl ether) (0.617 g, 62%).

¹H NMR (CDCl₃): =7.66(d, J=7.6 Hz, 1H, Ph), 7.59(d, J=7.6 Hz, 2H, Ph^(Ts)), 7.21 (t, J=7.6 Hz, 1H, Ph), 7.15(d, J=7.6 Hz, 2H, Ph^(Ts)), 7.02 (t, J=7.6 Hz, 1H, Ph), 6.90 (d, J=7.6 Hz, 1H, Ph), 6.64(s, 1H, NH), 5.93(s, 1H, CH^(Cp)), 3.09-2.85(m, 2H, CH₂), 2.36(s, 3H, CH₃), 1.67(s, 3H, CH₃), 1.38(s, 3H, CH₃); ¹³C {¹H} NMR (CDCl₃): =143.57, 142.00, 142.16, 137.32, 134.07, 134.55, 129.90, 129.32, 129.12, 127.95, 126.95, 125.38, 123.59, 118.11, 44.50, 21.46, 14.36, 14.05

EXAMPLE 29 2-(2,5-dimethylcyclopenta-1,4-dienyl)-4-fluorophenyl(p-toluenesulfonyl)amine

The same experiment as in Example 17 was carried out, using 1.000 g (2.93 mmol) of 2-(2-(p-toluenesulfonyl)amino-4-fluorophenyl)-3-methyl-2-cyclopenten-1-one and 3.660 ml (5.860 mmol) of MeLi (1.6 M in diethyl ether) (0.210 g, 53%).

¹H NMR (CDCl₃): =7.62(d, J=8.0 Hz, 2H, Ph^(Ts)), 7.20(d, J=8.0 Hz, 2H, Ph^(Ts)), 6.81-6.76(m, 1H, Ph), 6.66-6.63(m, 1H, Ph), 6.45(s, 1H, NH), 5.87(d, J=1.6 Hz, 1H, CH^(Cp)), 2.87-2.72(m, 2H, CH₂), 2.42(s, 3H, CH₃), 1.82(s, 3H, CH₃), 1.72(d, J=2.0 Hz, 3H, CH₃); ¹³C {¹H} NMR (CDCl₃): =161.36, 159.38, 158.89, 156.79, 143.05, 142.65, 141.84, 137.36, 128.93, 126.64, 124.79, 118.94, 112.73, 103.09, 44.30, 21.45, 14.69, 14.44

EXAMPLE 30 phenylene(p-toluenesulfonylamido)(2,5-dimethylcyclopentadienyl)titanium bis(dimethylamide)

The same experiment as in Example 17 was carried out, using 0.500 g (1.473 mmol) of 2-(2,5-dimethylcyclopenta-1,4-dienyl)phenyl(p-toluenesulfonyl)amine, and 0.330 g (1.473 mmol) of Ti(NMe₂)₄. The crylstaine structure of the product is shown in FIG. 1.

¹H NMR (C₃D₃): =8.12(d, J=8.0 Hz, 1H, Ph), 7.80(d, J=7.6 Hz, 2H, Ph^(Ts)), 7.14 (t, J=8.0 Hz, 1H, Ph), 6.97(d, J=8.0 Hz, 1H, Ph), 6.84(t, J=8.0 Hz, 1H, Ph), 6.74(d, J=8.0 Hz, 2H, Ph^(Ts)), 5.74(s, 2H, CH^(Cp)), 3.28(s, 12H, N—CH₃), 1.86(s, 3H, CH₃), 1.67(s, 6H, CH₃*2)

EXAMPLE 31 4-fluorophenylene(p-toluenesulfonylamido)(2,5-dimethylcyclopentadienyltitanium bis(dimethylamide)

The same experiment as in Example 24 was carried out, using 0.146 g (0.389 mmol) of 2-(2,5-dimethylcyclopenta-1,4-dienyl)-4-fluorophenyl(p-toluenesulfonyl)amine, and 0.087 g (0.389 mmol) of Ti(NMe₂)₄.

¹H NMR (C₃D₃): =8.22(d, J=8.0 Hz, 2H, Ph^(Ts)), 6.87(d, J=8.0 Hz, 2H, Ph^(Ts)), 6.65(d, J=7.6 Hz, 1H, Ph), 6.50(t, J=7.6 Hz, 1H, Ph), 5.86(s, 2H, CH^(Cp)), 3.28(s, 12H, N—CH₃), 1.94(s, 3H,CH₃), 1.89(s, 6H,CH₃*2)

EXAMPLE 32 phenylene(2-mesitylenesulfonylamido)(2,5-dimethylcyclopentadienyl)titanium dichloride

0.200 g (0.426 mmol) of C₆H₄(2,4,6-Me₃PhSO₂N)(2,5-Me₂Cp)Ti(NMe₂)₂ (in situ chlorinated after NMR measuring) metled in 3 mL of toluene and 0.211 g (1.634 mmol) of Me₂SiCl₂ diluted in 1 mL of toluene were loaded to a 20 mL vial, and then reacted for 1 hour. Toluene contined in the reaction product was removed in vaccum. The resultant product was solidated using pentane (0.190 g, 72%).

¹H NMR (C₃D₃): =6.84(m, 3H, Ph), 6.56(s, 2H, CH^(Cp)), 6.54(d, J=7.6 Hz, 1H, Ph), 6.52(s, 2H, Ph^(Mes)), 2.60(s, 6H,CH₃*2), 1.88(s, 3H,CH₃), 1.82(s, 6H,CH₃*2); ¹³C {¹H} NMR (C₃D₃): =155.58, 143.37, 143.22, 139.83, 139.32, 132.47, 129.78, 128.53, 126.20, 124.60, 124.04, 114.54, 23.61, 20.93, 15.04

EXAMPLE 33 5-fluorophenylene(2-mesitylenesulfonylamido)(2,5-dimethylcyclopenta-dienyl)titanium dichloride

The same expresiemnt as in Example 32 was carried out, using 0.182 g of 5-FC₆H₃(2,4,6-Me₃PhSO₂N)(2,5-Me₂Cp)Ti(NMe₂)₂ (in situ chlorinated after NMR measuring) and 0.161 g (1.245 mmol) of Me₂SiCl₂. The product was measured by NM R spectroscopy, but was not identified.

EXAMPLE 34 4-fluorophenylene(2-mesitylenesulfonylamido)(2,5-dimethylcyclopenta-dienyl)titanium dichloride

The same expresiemnt as in Example 32 was carried out, using 0.170 g of 4-FC₆H₃(2,4,6-Me₃PhSO₂N)(2,5-Me₂Cp)Ti(NMe₂)₂ (in situ chlorinated after NMR measuring) and 0.152 g (1.176 mmol) of Me₂SiCl₂. The product was measured by NMR spectroscopy, but was not identified.

EXAMPLE 35 phenylene(p-toluenesulfonylamido)(2,5-dimethylcyclopentadienyl)titanium dichloride

The same expresiemnt as in Example 32 was carried out, using 0.150 g (0.317 mmol) of C₆H₄(4-MePhSO₂N)(2,5-Me₂Cp)Ti(NMe₂)₂ and 0.123 g (0.951 mmol) of Me₂SiCl₂ (0.130 g, 88%).

¹H NMR (C₃D₃): =8.14(d, J=7.6 Hz, 2H, Ph^(Ts)), 7.09(d, J=7.6 Hz, 2H, Ph), 6.94 (t, J=7.6 Hz, 1H, Ph), 6.80(t, J=7.6 Hz, 1H, Ph), 6.74(d, J=7.6 Hz, 1H, Ph), 6.61(d, J=7.6 Hz, 2H, Ph^(Ts)), 6.59(s, 2H, CH^(Cp)), 1.75(s, 6H, CH₃*2), 1.73.(s, 3H, CH₃)

EXAMPLE 36 4-fluorophenylene(p-toluenesulfonylamido)(2,5-dimethylcyclopentadienyl)titanium dichloride

The same expresiemnt as in Example 32 was carried out, using 0.102 g (0.200 mmol) of 4-FC₆H₄(4-MePhSO₂N)(2,5-Me₂Cp)Ti(NMe₂)₂ and 0.077 g (0.601 mmol) of Me₂SiCl₂ (0.080 g, 81%).

¹H NMR (C₃D₃): =8.18(d, J=8.0 Hz, 2H, Ph^(Ts)), 6.73(d, 1H, CH^(Cp)), 6.65(d, J=8.0 Hz, 2H, Ph^(Ts)), 6.54(d, 1H, CH^(Cp)), 6.27-6.21(m, 1H, Ph), 6.14-6.12(m, 1H, Ph), 1.84(s, 3H,CH₃), 1.79(s, 3H,CH₃), 1.66(s, 3H,CH₃)

EXAMPLE 37 2-(2,5-dimethylcyclopenta-1,4-dienyl)phenyl(methanesulfonyl)amine

2-(2,5-dimethylcyclopenta-1,4-dienyl)phenylamine (0.500 g, 2.699 mmol) was melted in 5 mL of M.C, and then 0.235 g (2.969 mmol) of pyridine and 0.340 g (2.969 mmol) of methanesulfonyl chloride were added thereto. The reactants were reacted at room temperature for 7 hours. Then, 4 mL of 2 N HCl and 10 mL of M.C were added to the reaction product. The organic layer was collected and dried over MgSO₄to remove water contained therein. The solvent contained in the resultant organic layer was removed using a rotary vaccum evaporator. The product was filtered uisng 10 mL of diethyl ether, thereby obtaining whilte solid (0.482 g, 68%).

¹H NMR (CDCl₃): δ 0.92 (d, J=1.6 Hz, 3H, CH₃), 1.89 (s, 3H, CH₃), 2.95 (s, 3H, CH₃), 2.99-3.13 (m, 2H, CH₂), 6.03 (d, J=1.6 Hz, 1H, CH), 6.45 (s, 1H, NH), 7.09 (dd, J=7.6, 1.6 Hz, 1H, Bz^(3 or 6)), 7.15 (td, J=7.6, 1.2 Hz, 1H, Bz^(4 or 5)), 7.33 (td, J=7.6, 1.6 Hz, 1H, Bz^(4 or 5)), 7.63 (d, J=7.6 Hz, 1H, Bz^(3 or 6)) ppm.

EXAMPLE 38 phenylene(methanesulfonylamido)(2,5-dimethylcyclopentadienyl)titanium bis(dimethylamide)

0.400 g (1.519 mmol) of 2-(2,5-dimethylcyclopenta-1,4-dienyl)phenyl (methanesulfonyl)amine and 0.341 g (1.519 mmol) of Ti(NMe₂)₄ were added to 12 mL of toluene, and then reacted at 50° C. for 12 hours. The solvent contained in the reaction product was removed in a reduced pressure. The resultant reaction product was filtered using 10 mL of pentane in a drybox and then dried in a reduced pressure, thereby obtaining red solid (0.507 g, 84%).

¹H NMR (C₆D₆): δ 1.63 (s, 6H, Cp-CH₃), 2.45 (s, 3H, CH₃), 3.11 (s, 12H, Ti(NMe₂)₃), 5.62 (s, 1H, CH), 6.94 (t, J=7.2 Hz, 1H, Bz^(4 or 5)), 6.94 (d, J=7.2 Hz, 1H, Bz^(3 or 6)), 7.16 (t, J=7.2 Hz, 1H, Bz^(4 or 5)), 8.04 (d, J=7.2 Hz, 1H, Bz^(3 or 6)) ppm.

EXAMPLE 39 phenylene(methanesulfonylamido)(2,5-dimethylcyclopentadienyl)titanium dichloride

0.400 g (1.007 mmol) of C₆H₄(MeSO₂N)(2,5-Me₂Cp)Ti(NMe₂)₂ and 0.390 g (3.020 mmol) Me₂SiCl₂ were added to 10 mL of toluene and then reacted at room temperature for one hour. By-products contained in the reaction product was removed in a reduced pressure. The resultant reaction product was filtered using 10 mL of pentane in a drybox and dried in a reduced pressure (0.298 g, 78%).

¹H NMR (C₆D₆): δ 1.62 (broad s, 6H, Cp-CH₃), 2.51 (s, 3H, CH₃), 6.41-6.62 (broad s, 1H, CH), 6.75 (d, J=7.2 Hz, 1H, Bz^(3 or 6)), 6.86 (t, J=7.2 Hz, 1H, Bz^(4 or 5)), 7.01 (t, J=7.2 Hz, 1H, Bz^(4 or 5)), 7.04 (d, J=7.2 Hz, 1H, Bz^(3 or 6))

EXAMPLE 40 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)phenyl(p-toluenesulfonyl)amine

0.131 g (1.505 mmol) of pyridine and 0.316 g (1.656 mmol) of p-toluenesulfonyl chloride were added to 0.300 g (1.505 mmol) of 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)phenylamine melted in 3 mL of MC, and then reacted at room temperature for 12 hours. 3 mL of 2 N HCl was added to the reaction product and strongly stirred for a few minutes. The organic layer was collected. The collected organic layer was neutralized with 3 mL of H₂O without delay and dried over MgSO₄. The product was filtered using a column chromatography with hexane/ethylacetate (v/v=3:1). The solvent contained in the puried product was dried in vacuum, thereby obtaining white solid (0.340 g, 64%).

¹H NMR (CDCl₃): δ 1.32(d, J=1.6 Hz, 3H, CH₃), 1.65(s, 3H, CH₃), 1.95(s, 3H, CH₃), 2.38(s, 3H, CH₃), 2.95(qd, J=19.2, 1.6 Hz, 2H, Cp-CH₂), 6.67(s, 1H, NH), 6.92 (dd, J=7.6, 1.6 Hz, 1H, Ph), 7.05 (td, J=7.6, 1.6 Hz, 1H, Ph), 7.15(d, J=8.0 Hz, 2H, Ts-Ph), 7.24 (td, J=7.6, 1.6 Hz, 1H, Ph), 7.62(d, J=8.0 Hz, 2H, Ts-Ph), 7.64(dd, J=7.6, 1.6 Hz, 1H, Ph) ppm. ¹³C{¹H} NMR(CDCl₃): δ 11.09, 14.05, 14.36, 21.46, 44.50, 118.11, 123.59, 125.38, 126.95, 127.95, 129.12, 129.32, 129.90, 134.55, 134.07, 137.32, 142.16, 142.00, 143.57 ppm.

EXAMPLE 41 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)-4,6-dimethylphenyl(p-toluenesulfonyl)amine

White solid was obtained in the same manner as in Example 40 using 0.699 g (3.075 mmol) of 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)-4,6-dimethylphenylamine, 0.243 g (3.075 mmol) of pyridine, and 0.645 g (3.383 mmol) of p-toluenesuffonyl chloride (1.009 g, 86%).

¹H NMR (CDCl₃): δ 1.26(d, J=0.8 Hz, 3H, Cp-CH₃), 1.58(s, 3H, Cp-CH₃), 1.71(s, 3H, Cp-CH₃), 2.20(s, 3H, Ph-CH₃), 2.31(s, 3H, Ph-CH₃), 2.37(s, 3H, Ts-CH₃), 2.26-2.58(m, 2H, Cp-CH₂), 5.95(s, 1H, NH₁), 6.54(s, 1H, Ph), 6.93(s, 1H, Ph), 7.03(d, J=8.0 Hz, 2H, Ts-Ph), 7.35(d, J=8.0 Hz, 2H, Ts-Ph) ppm.

EXAMPLE 42 2-(2,3,5-Ttrimethylcyclopenta-1,4-dienyl)-4,6-difluorophenyl(p-toluenesulfonyl)amine

White solid was obtained in the same manner as in Example 40 using 0.300 g (1.275 mmol) 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)-4,6-difluorophenylamine, 0.101 g (1.275 mmol) of pyridine, and 0.267 g (1.403 mmol)p-toluenesulfonyl chloride (0.340 g, 68%).

¹H NMR (CDCl₃): δ 1.53(d, J=1.2 Hz, 3H, Cp-CH₃), 1.78(s, 3H, Cp-CH₃), 1.88(s, 3H, Cp-CH₃), 2.43(s, 3H, Ts-CH₃), 3.96(qd, J=23.2, 1.6 Hz, 2H, Cp-CH₂), 6.26(s, 1H, NH₁), 6.60-6.63(m, 1H, Ph), 6.77-6.83(m, 1H, Ph), 7.21(d, J=8.4 Hz, 2H, Ts-Ph), 7.62(d, J=8.4 Hz, 2H, Ts-Ph) ppm. ¹³C{¹H} NMR(CDCl₃): δ 11.66, 13.48, 14.46, 21.61, 48.78, 103.19, 112.70, 118.94, 126.74, 128.94, 133.91, 133.98, 137.40, 137.48, 138.36, 143.04, 156.58, 158.97, 161.32 ppm.

EXAMPLE 43 phenylene(p-toluenesulfonylamido)(2,3,5-trimethylcyclopentadienyl)titanium bis(dimethylamide)

0.201 g (0.569 mmol) of 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)phenyl(p-toluenesulfonyl)amine and 0.128 g (0.569 mmol) of Ti(NMe₂)₄ were added to 6 mL of toluene, and then reacted at 70° C. for 12 hours. The reaction product was dried to revmoe all the entire volatile materials in vacuum, and then washed using 5 mL of pentane, thereby obtaining red solid.

¹H NMR (C₆D₆): δ 1.64(s, 3H, CH₃), 1.70(s, 3H, CH₃), 1.83(s, 3H, CH₃), 1.89(s, 3H, CH₃), 3.09(s, 6H, Ti—NMe₂), 3.50(s, 6H, Ti—NMe₂), 5.95(s, 1H, Cp-CH), 6.76(d, J=7.6 Hz, 2H, Ts-Ph), 6.83(t, J=8.0 Hz, 1H, Ph), 6.98(d, J=8.0 Hz, 1H, Ph), 7.11 (t, J=8.0 Hz, 1H, Ph), 7.77(d, J=7.6 Hz, 2H, Ts-Ph), 8.07(d, J=8.0 Hz, 1H, Ph) ppm

EXAMPLE 44 4,6-dimethylphenylene(p-toluenesulfonylamido)(2,3,5-trimethylcyclopenta-dienyl)titanium bis(dimethylamide)

Red solid was obtained in the same manner as in Example 43 using 0.303 g (0.794 mmol) of 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)-4,6-dimethylphenyl(p-toluenesulfonyl)amine and 0.179 g (0.794 mmol) of Ti(NMe₂)₄.

¹H NMR (C₆D₆): δ 1.88(s, 3H, CH₃), 1.95(s, 3H, CH₃), 2.06(s, 3H, CH₃), 2.14(s, 3H, CH₃), 2.19(s, 3H, CH₃), 3.23(s, 6H, Ti—Me₂), 3.43(s, 6H, Ti—Me₂), 5.93(s, 1H, Cp-CH), 6.77(s, 1H, Ph), 6.85(d, J=5.6 Hz, 2H, Ts-Ph), 6.96(s, 1H, Ph), 8.23(d, J=5.6 Hz, 2H, Ts-Ph) ppm. ¹³C{¹H} NMR(C₆D₆): δ 11.69, 13.06, 13.44, 20.60, 21.10, 21.40, 51.89, 52.49, 113.91, 120.39, 121.87, 126.87, 127.83, 129.42, 131.49, 131.61, 132.72, 133.36, 134.33, 141.97, 142.48, 146.53 ppm

EXAMPLE 45 4,6-fluorophenylene(p-toluenesulfonylamido)(2,3,5-trimethylcyclopenta-dienyl)titanium bis(dimethylamide)

Red solid was obtained in the same manner as in Example 43 using 0.166 g (0.426 mmol) of 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)-4,6-fluorophenyl(p-toluenesulfonyl)amine and 0.095 g (0.426 mmol) ofTi(NMe₂)₄.

¹H NMR (C₆D₆): δ 1.65(s, 3H, CH₃), 1.88(s, 3H, CH₃), 1.94(s, 3H, CH₃), 1.99(s, 3H, CH₃), 3.07(s, 6H, Ti—Me₂), 3.39(s, 6H, Ti—Me₂), 5.83(s, 1H, Cp-CH₁), 6.43-6.49(m, 1H, Ph), 6.60-6.63(m, 1H, Ph), 6.81 (d, J=8.0 Hz, 2H, Ts-Ph), 8.16(d, J=8.4 Hz, 2H, Ts-Ph) ppm. ¹³C{¹H} NMR(C₆D₆): δ 11.26, 12.77, 13.00, 21.38, 51.82, 52.74, 104.12, 112.12, 114.39, 119.65, 120.24, 121.52, 127.01, 129.40, 131.91, 141.09, 142.35, 153.34, 155.80, 157.51, 159.93 ppm

EXAMPLE 46 phenylene(p-toluenesulfonylamido)(2,3,5-trimethylcyclopentadienyl)titanium dichloride

0.228 g (1.707 mmol) of dichlorodimethylsilane and 4 ml of toluene were added to C₆H₄(4-MePhSO₂N)(2,3,5-Me₃Cp)Ti(NMe₂)₂ that was obtained in Example 43, and then reacted at room temperature for 1 hour. The reaction product was dried to remove the volatile material in vacuum, and then washed using 3 mL of pentane, thereby obtaining yellow solid (0.228 g, 78%).

¹H NMR (C₆D₆): δ 1.66(br s, 3H, CH₃), 1.79(s, 6H, CH₃), 2.26(s, 3H, CH₃), 6.48(s, 1H, Cp-CH), 6.66(d, J=8.0 Hz, 2H, Ts-Ph), 6.86-6.88(m, 2H, Ph), 6.99-7.02(m, 1H, Ph), 7.11-7.13(m, 2H, Ph), 8.16(d, J=8.0 Hz, 2H, Ts-Ph) ppm. ¹³C{¹H} NMR(C₆D₆): δ 12.80, 15.19, 15.44, 21.41, 114.60, 124.57, 124.62, 125.63, 126.84, 128.50, 128.92, 129.27, 129.71, 130.01, 135.61, 135.69, 145.03, 155.27 ppm.

EXAMPLE 47 4,6-dimethylphenylene(p-toluenesulfonylamido)(2,3,5-trimethylcyclopentadienyl)titanium dichloride

0.307 g (2.382 mmol) of dichlorodimethylsilane and 8 mL of toluene were added to 4,6-Me₂C₆H₄(4-MePhSO₂N)(2,3,5-Me₃Cp)Ti(NMe₂)₂ that was obtained in Example 44, and then reacted at room temperature for one hour. The reaction product was dried in vacuum to remove the volatile material contained therein, and then washed using 9 mL of pentane, thereby obtaining yellow solid (0.327 g, 76%). ¹H NMR (C₆D₆): δ 1.80(s, CH₃), 1.84(s, CH₃), 1.90(s, CH₃), 1.92(s, CH₃), 1.95(s, CH₃), 2.11(s, CH₃), 2.13(s, CH₃), 2.15(s, CH₃), 2.28(s, CH₃), 2.29(s, CH₃), 2.39(s, CH₃), 6.38(s, Cp-CH), 6.51(s, Cp-CH), 6.61-6.64(m, 2H, Ts-Ph), 6.64(s, 2H, Ph), 8.08-8.12(m, 2H, Ts-Ph) ppm.

EXAMPLE 48 4,6-fluorophenylene(p-toluenesulfonylamido)(2,3,5-trimethylcyclopentadienyl)titanium dichloride

0.165 g (1.278 mmol) of dichlorodimethylsilane and 4 ml of toluene were added to 4,6-F₂C₆H₄(4-MePhSO₂N)(2,3,5-Me₃Cp)Ti(NMe₂)₂ that was obtained in Example 45, and then reacted at room temperature for one hour. The reaction product was dried in vacuum to remove the volatile material contained therein, and then washed using 4 mL of pentane, thereby obtaining yellow solid (0.166 g, 71%).

¹H NMR (C₆D₆): δ 1.61(s, 1.5H, CH₃), 1.72(s, 1.5H, CH₃), 1.81(s, 1.5H, CH₃), 1.82(s, 1.5H, CH₃), 1.83(s, 1.5H, CH₃), 1.90(s, 1.5H, CH₃), 2.28(s, 3H, CH₃), 6.26-6.32(m, 2H, Ph), 6.46(s, 0.5H, Cp-CH₁), 6.63(s, 0.5H, Cp-CH₁), 6.70(d, J=8.0 Hz, 2H, Ts-Ph), 8.17-8.20(m, 2H, Ts-Ph) ppm.

EXAMPLE 49 2-(2,5-dimethylcyclopenta-1,4-dienyl)phenyl(trimethylacetyl)amine

0.130 g (1.29 mmol) of triethylamine and 0.155 g (1.29 mmol) of pivaloyl chloride were added to 0.263 g (1.42 mmol) of 2-(2,5-dimethylcyclopenta-1,4-dienyl)phenylamine solution melted in 10 mL of MC solvent, and then reacted at room temperature for 1 hour. 5 mL of 2N HCl was added to the reaction product and strongly stirred for a few minutes. The organic layer was neutralized using 5 mL of NaHCO₃, and the product was filtered using a column chromatography with a hexane/ethyl acetate (v/v, 10:1) solvent. The refined product was dried in vaccum to remove the solvent therein, thereby obtaining while solid (0.355 g, 93%).

¹H NMR (CDCl₃): 1.18 (s, 9H, C(CH₃)₃), 1.73 (q, J=1.6 Hz, 3 H, Cp-CH₃), 1.89 (s, 3H, Cp-CH₃), 3.08-3.07 (m, 2 H, Cp-CH₂), 6.05 (d, J=2.0 Hz, 1 H, Cp-CH), 7.07 (dd, 1 H, J=7.6, 2.0 Hz, 1 H, bz-CH), 7.11 (td, J=7.2, 1.2 Hz, 1 H, bz-CH), 7.33 (td, J=8.4, 2.0 Hz, 1 H, bz-CH), 7.54(s, 1 H, NH), 8.44 (d, J=8.0 Hz, 1 H, bz-CH) ppm; ¹³C{¹H} NMR(CDCl₃): 14.47, 14.64, 27.42, 39.84, 44.59, 119.15, 123.14, 125.27, 128.07, 129.28, 136.02, 138.36, 142.64, 142.76, 175.93 ppm.

EXAMPLE 50 2-(2,5-dimethylcyclopenta-1,4-dienyl)-3,5-dimethylphenyl(trimethylacetyl)amine

An experiment was performed in the same manner as in Example 49 using 0.717 g (3.36 mmol) of 2-(2,5-dimethylcyclopenta-1,4-dienyl)-3,5-dimethylphenylamine, 0.408 g (4.03 mmol) of triethylamine, and 0.486 g (4.03 mmol) of pivaloyl chloride. The reaction product was filtered using a column chromatography with a toluene/MC (v/v, 1:1) solvent. The resultant reaction product was dried in vacuum to remove the solvent therein, thereby obtaining while solid (0.698 g, 70%).

¹H NMR (CDCl₃): 1.17 (s, 9 H,C(CH₃)₃), 1.69 (s, 3 H, Cp-CH₃), 1.85 (s, 3H, Cp-CH₃), 2.24 (s, 3 H, bz-CH₃), 2.34(s, 3 H, bz-CH₃), 2.97(d, J=1.2 Hz, 2 H, Cp-CH₂), 5.94 (s, 1 H, Cp-CH), 6.75 (s, 1 H, NH), 6.78 (s, 1 H, bz-CH), 7.03 (s, 1 H, bz-CH) ppm; ¹³C{¹H} NMR(CDCl₃): 14.54, 14.58, 18.74, 21.08, 27.50, 44.19, 123.88, 127.76, 130.41, 131.19, 132.90, 134.94, 135.59, 140.14, 143.35, 175.85 ppm.

EXAMPLE 51 2-(2,5-dimethylcyclopenta-1,4-dienyl)-3,5-fluorophenyl(trimethylacetyl)amine

Yellow solid was obtained in the same manner as in Example 49 using 0.402 g (1.82 mmol) of 2-(2,5-dimethylcyclopenta-1,4-dienyl)-3,5-fluorophenylamine, 0.202 g (2.18 mmol) of triethylamine, and 0.263 g (2.18 mmol) of pivaloyl chloride (0.347 g, 66%).

¹H NMR (C₆D₆): 1.01 (s, 9 H, C(CH₃)₃), 1.66 (s, 3H, Cp-CH₃), 1.72 (q, J=2.0 Hz, 3 H, Cp-CH₃), 2.65-2.67 (m, 2 H, Cp-CH₂ ), 5.79 (d, J=2.0 Hz, 1 H, Cp-CH), 6.36 (s, 1 H, NH), 6.52 (s, 1 H, bz-CH), 6.54 (s, 1 H, bz-CH) ppm; ¹³C{¹H} NMR(C₆D₆): 14.60, 14.63, 27.57, 39.28, 44.53, 103.58 (t, J=102.8 Hz, 1C, bz-C—F), 112.41 (dd, J=84.8, 15.2 Hz, bz-C—F), 124.60, 141.70, 142.95, 157.34 (d, J=51.6 Hz, 1C, bz-C—F), 159.62 (d, J=51.6 Hz, 1C, bz-C—F), 159.84 (d, J=54.8 Hz, 1C, bz-C—F), 162.09 (d, J=48.8 Hz, 1C, bz-C—F), 175.52 ppm.

EXAMPLE 52 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)phenyl(trimethylacetyl)amine

An experiment was performed in the same manner as in Example 49 using 0.534 g (2.68 mmol) of 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)phenylamine, 0.325 g (3.22 mmol) of triethylamine, and 0.388 g (3.22 mmol) of pivaloyl chloride. The reaction product was purified using a column chromatography with a hexane/ethylacetate (v/v, 5:1) solvent. The purified product was dried in vaccum to remove the solvent therein, thereby obtaining while solid (0.674 g, 89%).

¹H NMR (CDCl₃): 1.17 (s, 9 H, C(CH₃)₃), 1.58 (s, 3 H, Cp-CH₃), 1.83 (s, 3H, Cp-CH₃), 1.98 (s, 3 H, Cp-CH₃), 3.01 (s, 2 H, Cp-CH₂ ), 7.05(dd, J=7.6, 2.0 Hz, 1 H, bz-CH), 7.08 (td, 1 H, J=7.6, 1.2 Hz, 1 H, bz-CH), 7.30 (td, J=7.6, 1.6 Hz, 1 H, bz-CH), 7.60(s, 1 H, NH), 8.44(d, J=8.4 Hz, 1 H, bz-CH) ppm; ¹³C{¹H} NMR(CDCl₃): 11.46, 13.51, 14.17, 27.29, 39.71, 48.87, 118.94, 122.96, 126.21, 127.78, 129.13, 134.27, 134.63, 135.91, 137.91, 137.92, 138.67, 175.75 ppm.

EXAMPLE 53 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)-4,6-dimethylphenyl(trimethylacetyl)amine

The same experiment as in Example 49 was performed using 0.600 g (2.64 mmol) of 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)-4,6-dimethylphenylamine, 0.321 g (3.17 mmol) of triethylamine, and 0.382 g (3.17 mmol) of pivaloyl chloride (0.727 g, 89%).

¹H NMR (CDCl₃): 1.16 (s, 9 H, C(CH₃)₃), 1.54 (s, 3 H, Cp-CH₃), 1.80 (s, 3H, Cp-CH₃), 1.94 (s, 3 H, Cp-CH₃), 2.23 (s, 3 H, bz-CH₃ ), 2.33 (s, 3 H, bz-CH₃), 2.91 (brd, J=5.6 Hz, 2 H, Cp-CH₂), 6.76 (s, 2 H, bz-CH), 7.02 (s, 1 H, NH) ppm; ¹³C{¹H} NMR(CDCl₃): 11.63, 13.50, 18.79, 21.09, 27.46, 39.13, 48.64, 127.68, 130.28, 131.18, 132.85, 133.22, 134.79, 135.34, 135.47, 135.62, 140.51, 175.77 ppm.

EXAMPLE 54 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)-4,6-difluorophenyl(trimethylacetyl)amine

The same experiment as in Example 49 was performed using 0.463 g (1.97 mmol) of 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)-4,6-fluorophenylamine, 0.239 g (2.36 mmol) of triethylamine, and 0.285 g (2.36 mmol) of pivaloyl chloride (0.400 g, 64%).

¹H NMR (CDCl₃): 1.18 (s, 9 H, C(CH₃)₃), 1.58 (s, 3 H, Cp-CH₃), 1.82 (s, 3H, Cp-CH₃), 1.94 (s, 3 H, Cp-CH₃), 2.92 (s, 2 H, Cp-CH₂), 6.61 (s, 1 H, NH), 6.67 (dq, J=8.4, 2.8 Hz, 1 H, bz-CH), 6.86 (td, 1 H, J=8.4, 2.4 Hz, 1 H, bz-CH) ppm; ¹³C{¹H} NMR(CDCl₃): 11.57, 13.48, 14.28, 27.45, 48.86, 103.26 (t, J=100.0 Hz, 1C, bz-C—F), 111.97 (dd, J=87.8, 12.4 Hz, 1C, bz-C—F), 133.71, 134.31, 137.47, 138.02, 156.19 (d, J=51.6 Hz, 1C, bz-C—F), 158.69 (d, J=51.6 Hz, 1C, bz-C—F), 158.99 (d, J=54.8 Hz, 1C, bz-C—F), 161.45 (d, J=51.6 Hz, 1C, bz-C—F), 176.00 ppm.

EXAMPLE 55 phenylene(t-butylcarboxyamido)(2,5-dimethylcyclopentadienyl)titanium bis(dimethylamide)

5 mL of toluene was added to 0.203 g (0.700 mmol) of 2-(2,5-dimethylcyclopenta-1,4-dienyl)phenyl(trimethylacetyl)amine and 0.156 g (0.700 mmol) of tetrakis(dimethylamino)titanium, and then the reaction solution was stirred at 80° C. for one day. The reaction product was dried in vacuum to remove the volatile material therein, thereby obtaining red oil. (100% purity was identified through ¹H and ¹³C NMR spectroscope).

¹H NMR (C₆D₆): 1.43 (s, 9 H,C(CH₃)₃), 1.94 (s, 6 H, Cp-CH₃), 2.97 (s, 12H, N—CH₃), 5.79 (s, 2 H, Cp-CH), 7.01(td, J=8.4, 1.2 Hz, bz-CH), 7.26 (t,d, J=8.4, 1.6 Hz, 1 H, bz-CH), 7.30(d, J=8.0 Hz, 1H, bz-CH), 7.66(d, J=8.0 Hz, 1 H, bz-CH) ppm; ¹³C{¹H} NMR(C₆D₆): 14.73 (Cp-CH₃), 29.14 (C(CH₃)₃), 39.77(C(CH₃)₃), 48.35 (N—CH₃), 112.35, 122.81, 125.21, 125.55, 128.54, 131.55, 132.86, 144.65, 168.49 ppm.

EXAMPLE 56 4,6-dimethylphenylene(t-butylcarboxamido)(2,5-dimethylcyclopentadienyl)titanium bis(dimethylamide)

7 mL of toluene solvent was added to 0.515 g (1.73 mmol) of 2-(2,5-dimethylcyclopenta-1,4-dienyl)-4,6-dimethylphenyl(trimethylacetyl)amine and 0.388 g (1.73 mmol) of tetrakis(dimethylamino)titanium. The reaction solution was stirred at 80° C. for 5 days, and then dired in vaccum to remove the volatile material therein, thereby obtaining red oil (almost 100% purity was identified through ¹H and ¹³C NMR spectroscope).

¹H NMR (C₆D₆): 1.43 (s, 9 H, C(CH₃)₃), 1.97 (s, 6 H, Cp-CH₃), 2.25 (s, 3 H, bz-CH₃), 2.62 (s, 3 H, bz-CH₃), 2.99 (s, 12 H, N—CH₃), 5.89 (s, 2 H, Cp-CH), 6.98(s, 1 H, bz-CH), 7.08 (s, 1 H, bz-CH) ppm; ¹³C{¹H} NMR(C₆D₆): 14.95, 21.15, 21.60, 29.29, 40.30, 48.42, 112.44, 122.68, 124.72, 125.78, 130.92, 131.22, 131.38, 136.98, 140.37, 167.22 ppm.

EXAMPLE 57 4,6-difluorophenylene(t-butylcarboxamido)(2,5-dimethylcyclopentadienyl)titanium bis(dimethylamide)

5 mL of toluene solvent was added to 0.277 g (0.87 mmol) of 2-(2,5-dimethylcyclopenta-1,4-dienyl)-4,6-difluorophenyl(trimethylacetyl)amine and 0.195 g (0.87 mmol) of tetrakis(dimethylamino)titanium. The reaction solution was stirred at 80° C. for one day, and then dried in vacuum to remove the volatile material therein, thereby obtaining red oil (almost 100% purity was identified through ¹H and ¹³C NMR spectroscope).

¹H NMR (C₆D₆): 1.37 (s, 9 H, C(CH₃)₃), 1.81 (s, 6 H, Cp-CH₃), 2.92 (s, 12H, N—CH₃), 5.79 (s, 2 H, Cp-CH), 6.69-6.78(m, 2 H, bz-CH) ppm; ¹³C{¹H} NMR(C₆D₆): 14.51, 29.04, 44.37, 48.29, 103.78 (t, J=108 Hz, 1C, bz-C—F), 112.59, 113.69 (dd, J=84.0, 15.2 Hz, 1C, bz-C—F), 123.08, 156.22 (d, J=51.6 Hz, 1C, bz-C—F), 157.52 (d, J=51.6 Hz, 1C, bz-C—F), 158.63 (d, J=51.2 Hz, 1C, bz-C—F), 160.48 (d, J=48.4 Hz, 1C, bz-C—F), 170.32 ppm.

EXAMPLE 58 phenylene(t-butylcarboxamido)(2,3,5-trimethylcyclopentadienyl)titanium bis(dimethylamide)

6 mL of toluene solvent was added to 0.486 g (1.72 mmol) of 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)phenyl(trimethylacetyl)amine and 0.386 g (1.72 mmol) of tetrakis(dimethylamino)titanium. The reaction solution was stirred at 80° C. for one day, and then the volatile material therein was removed, thereby obtaining red oil (100% purity was identified through ¹H and ¹³C NMR spectroscope).

¹H NMR (C₆D₆): 1.45 (s, 9 H, C(CH₃)₃), 1.88(s, 3 H, Cp-CH₃), 1.94 (s, 3 H, Cp-CH₃), 2.03 (s, 3 H, Cp-CH₃), 2.81 (s, 6 H, N—CH₃), 3.14 (s, 3 H, N—CH₃), 5.86 (s, 1 H, Cp-CH), 7.03 (td, J=7.2, 1.2 Hz, 1 H, bz-CH), 7.27 (dd, J=7.6, 0.8 Hz, 1 H, bz-CH), 7.30 (td, J=7.6, 1.2 Hz, 1 H, bz-CH), 7.70 (dd, J=8.0, 0.8 Hz, 1 H, bz-CH) ppm; ¹³C{¹H} NMR(C₆D₆): 12.79, 13.06, 14.13, 29.12, 39.76, 47.12, 49.85, 115.52, 120.22, 121.21, 121.31, 122.78, 125.59, 125.95, 128.48, 131.52, 132.95, 144.69, 168.90 ppm.

EXAMPLE 59 4,6-dimethylphenylene(t-butylcarboxamido)(2,3,5-trimethylcyclopentadienyl)titanium bis(dimethylamide)

7 mL of toluene solvent was added to 0.565 g (1.81 mmol) of 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)-4,6-dimethylphenyl(trimethylacetyl)amine and 0.407 g (1.81 mmol) of tetrakis(dimethylamino)titanium. The reaction solution was stirred at 110° C. for four days, and then the volatile material therein was removed, thereby obtaining red oil (almost 100% purity was identified through ¹H and ¹³C NMR spectroscope).

¹H NMR (C₆D₆): 1.45 (s, 9 H, C(CH₃)₃), 1.92 (s, 3 H, Cp-CH₃), 1.99 (s, 3H, Cp-CH₃), 2.06 (s, 3 H, Cp-CH₃), 2.27 (s, 3 H, bz-CH₃), 2.66 (s, 3 H, bz-CH₃), 2.83(s, 6 H, N—CH₃), 3.17(s, 6 H, N—CH₃), 5.89 (s, 1 H, Cp-CH), 6.99 (s, 1 H, bz-CH), 7.10 (s, 1H, bz-CH) ppm; ¹³C{¹H} NMR(C₆D₆): 12.85, 13.29, 14.37, 21.19, 21.57, 29.26, 40.28, 47.22, 49.98, 115.62, 119.81, 120.77, 121.33, 125.13, 126.11, 130.89, 131.13, 131.46, 136.96, 140.39, 167.63 ppm.

EXAMPLE 60 4,6-difluorophenylene(t-butylcarboxamido)(2,3,5-trimethylcyclopentadienyl)titanium bis(dimethylamide)

5 mL of toluene solvent was added to 0.277 g (0.87 mmol) of 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)-4,6-difluorophenyl(trimethylacetyl)amine and 0.195 g (0.87 mmol) of tetrakis(dimethylamino)titanium. The reaction solution was stirred at 80° C. for one day, and then the volatile material therein was removed, thereby obtaining red oil (almost 100% purity was identified through ¹H and ¹³C NMR spectroscope).

¹H NMR (C₆D₆): 1.41 (s, 9 H, C(CH₃)₃), 1.72 (s, 3 H, Cp-CH₃), 1.84 (s, 3 H, Cp-CH₃), 2.77 (s, 6 H, N—CH₃), 3.09(s, 3 H, N—CH₃), 5.08 (s, 1 H, Cp-CH), 6.73-6.79 (m, 2 H, bz-CH) ppm; ¹³C{¹H} NMR(C₆D₆): 12.67, 12.80, 14.01, 29.04, 40.28, 47.11, 49.82, 103.67 (t, J=102.8 Hz, 1C, bz-C—F), 112.75 (dd, J=84.8, 15.2 Hz, 1C, bz-C—F), 120.08, 121.24, 121.74, 123.17, 156.24 (d, J=54.4 Hz, 1C, bz-C—F), 160.51 (d, J=51.6 Hz, 1C, bz-C—F), 170.67 ppm.

EXAMPLE 61 4,6-dimethylphenylene(t-butylcarboxamido)(2,5-dimethylcyclopentadienyl)titanium (chloride)(dimethylamide)

0.515 g (1.73 mmol) of 2-(2,5-dimethylcyclopenta-1,4-dienyl)-4,6-dimethylphenyl-(trimethylacetyl)amine and 0.388 g (1.73 mmol) of Ti(NMe₂)₄ were added to 7 mL of toluene, and then reacted at 80° C. for 5 days. The reaction product was dried in vacuum to revmoe the entire solvent, thereby obtaining red oil (100% purity was identified through NMR spectroscophy).

¹H NMR (C₆D₆): 1.45 (s, 9H, C(CH₃)₃), 1.99 (s, 6H, CH₃), 2.26 (s, 3H, Ph-CH₃), 2.66 (s, 3H, Ph-CH₃), 2.99 (s, 12H, N—CH₃), 5.88 (s, 2H, Cp-H), 7.01 (s, 1H, Ph-H), 7.10 (s, 1H, Ph-H) ppm. ¹³C{¹H} NMR(C₆D₆): 14.95, 21.13, 21.62, 29.27, 40.31, 48.41, 112.42, 122.68, 124.75, 125.76, 130.97, 131.25, 131.40, 137.03, 140.39, 167.26 ppm.

7 mL of toluene and 10 mL of Me₂SiCl₂ were added to the obtained bis(dimethylamido)titanium and then reacted at 80° C. for one day. The reaction product was dried in vacuum to remove the entire volatile material, and then washed using 10 mL of pentane, thereby obtaining red solid (0.340 g, 45%).

¹H NMR (C₆D₆): 1.01 (s, 9H, C(CH₃)₃), 1.95 (s, 3H, Ph-CH₃), 2.02 (s, 6H, Cp-CH₃), 2.18 (s, 3H, N—CH₃), 2.23 (s, 3H, N—CH₃), 2.43 (s, 3H, Ph-CH₃), 6.00 (d, J=2.8 Hz, 1H, Cp-H), 6.25 (d, J=2.8 Hz, 1H, Cp-H), 6.83(s, 1H, Ph-CH), 7.44(s, 1H, Ph-H) ppm. ¹³C NMR(C₆D₆): 17.42, 18.27, 18.93, 21.05, 30.27, 39.91, 40.82, 122.49, 123.52, 124.25, 130.03, 132.01, 137.31, 141.55, 145.65, 147.44, 163.65 ppm.

EXAMPLE 62 phenylene(t-butylcarboxamido)(2,3,5-trimethylcyclopentadienyl)titanium (chloride)(dimethylamide)

The same experiment as in Example 61 was carried out, using 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)phenyl(trimethylacetyl)amine

EXAMPLE 63 4,6-difluorophenylene(t-butylcarboxamido)(2,3,5-trimethylcyclopentadienyl)titanium (chloride)(dimethylamide)

The same experiment as in Example 61 was carried out, using 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)-4,6-difluorophenyl(trimethylacetyl)amine.

EXAMPLE 64 4,6-difluorophenylene(t-butyliminooxy)(2,5-dimethylcyclopentadienyl)titanium dichloride

0.271 g (2.10 mmol) of dichlorodimethylsilane and 5 mL of toluene were added to 4,6-F₂C₆H₂(t-BuCON)(2,5-Me₂Cp)Ti(NMe₂)₂. The reaction solution was stirred at room temperature for 1 hour. The reaction product was dried in vacuum to remove the volatile material therein, washed using 10 mL of pentane solvent, and then dried in vaccum to remove the solvent, thereby obtaining yellow solid. (0.177 g, 60%). The crystalline structure of the product is illustrated in FIG. 2.

¹H NMR (C₆D₆): 1.33 (s, 9 H,C(CH₃)₃), 1.81 (s, 6 H, Cp-CH₃), 6.08 (s, 2H, Cp-CH), 6.15 (dq, J=9.2, 3.2 Hz, 1 H, bz-CH ), 6.54 (tdq, J=8.4, 3.6, 3.2 Hz, 1 H, bz-CH) ppm; ¹³C{¹H} NMR(C₆D₆): 16.42, 28.64, 42.10, 103.20 (t, J=103.2 Hz, 1C, bz-C—F), 113.85 (dd, J=92.0, 15.2 Hz, 1C, bz-C—F), 122.46, 132.43, 157.69 (d, J=51.6 Hz, 1C, bz-C—F), 158.59 (d, J=51.6 Hz, 1C, bz-C—F), 160.15 (d, J=54.8 Hz, 1C, bz-C—F), 161.09 (d, J=51.6 Hz, 1C, bz-C—F), 168.29 ppm.

EXAMPLE 65 (4,6-difluoro)phenylene(t-butyliminooxy)(2,3,5-trimethylcyclopentadienyl)titanium dichloride

0.377 g (2.61 mmol) of dichlorodimethylsilane and 5 mL of toluene were added to 4,6-F₂C₆H₂(t-BuCON)(2,3,5-Me₃Cp)Ti(NMe₂)₂. The reaction solution was stirred at room temperature for 8 hours. The reaction product was dried in vacuum to remove the volatile material, washed using 10 mL of pentane solvent and then dried in vaccum to remove the solvent, thereby obtaining yellow solid (0.378 g, 89%).

¹H NMR (C₆D₆): 1.34 (s, 9 H, C(CH₃)₃), 1.74 (s, 3 H, Cp-CH₃), 1.89 (s, 3 H, Cp-CH₃), 2.03 (s, 3 H, Cp-CH₃), 5.91 (s, 1 H, Cp-CH), 6.24 (dt, J=9.2, 2.4 Hz, 1 H, bz-CH), 6.57(tdt, J=8.4, 3.6, 2.0 Hz, 1 H, bz-CH) ppm; ¹³C{¹H} NMR(C₆D₆): 14.12, 15.58, 16.69, 28.66, 42.04, 105.39 (t, J=103.2 Hz, 1C, bz-C—F), 113.76 (dd, J=92.0, 18.0 Hz, 1C, bz-C—F), 123.83, 130.68, 131.35, 135.90, 157.67 (d, J=51.6 Hz, 1C, bz-C—F), 158.67 (d, J=51.6 Hz, 1C, bz-C—F), 160.12 (d, J=54.8 Hz, 1C, bz-C—F), 161.17 (d, J=51.6 Hz, 1C, bz-C—F),168.69, 175.45 ppm.

EXAMPLE 66 phenylene(t-butylcarboxamido)(2,5-dimethylcyclopentadienyl)dilithium salt

1.31 g (4.86 mmol) of 2-(2,5-dimethylcyclopenta-1,4-dienyl)phenyl(trimethylacetyl)amine was melted in 25 mL of diethyl ether. Then, 2.70 g of nBuLi (2.5 M in hexane) was slowly added thereto at −30° C. and stirred at room temperature for 6 hours. The reaction product was filtered using 10 mL of diethyl ether, and the used solvent was removed, thereby obtaining yellow salt in which the number of coordinated diethyl ethers was 0.39. (1.33 g, 89%).

¹H NMR (C₅D₅N): δ 1.35 (s, 9H, C(CH₃)₃), 2.26 (s, 6H, CH₃), 6.28 (s, 2H, Cp-H), 6.90 (td, J=6.8, 1.6 Hz, 1H, H^(4 or 5)), 7.01 (td, J=7.2, 1.6 Hz, 1H, H^(4 or 5)), 7.76 (dd, J=7.6, 2.4 Hz, 1H, H^(3 or 6)), 7.89 (d, J=8.0 Hz, 1H, H^(3 or 6)) ppm. ¹³C{¹H} NMR(C₅D₅N): δ 15.57, 29.86, 39.81, 103.50, 113.58, 115.13, 119.70, 123.99, 126.33, 131.13, 137.79, 153.18, 178.54 ppm.

EXAMPLE 67 phenylene(t-butylcarboxamido)(2,3,5-trimethylcyclopentadienyl)dilithium salt

An experiment in the same as Example 66 was carried out, using 1.28 g (4.52 mmol) of 2-(2,3,5-trimethylcyclopenta-1,4-dienyl)phenyl-(trimethylacetyl)amine. As a result, a yellow salt in which the number of coordinated diethyl ethers was 0.29. (1.40 g, 92%).

¹H NMR (C₅D₅N): δ 1.35 (s, 9H, C(CH₃)₃), 2.12 (s, 3H, CH₃), 2.28 (s, 3H, CH₃), 2.45 (s, 3H, CH₃), 6.11 (s, 1H, Cp-H), 6.90 (t, J=6.8 Hz, 1H, H^(4 or 5)), 7.02 (t, J=7.2 Hz, 1H, H^(4 or 5)), 7.76 (d, J=7.6 Hz, 1H, H^(3 or 6)), 7.89 (d, J=7.6 Hz, 1H, H^(3 or 6)) ppm. ¹³C{¹H} NMR(C₅D₅N): δ 12.90, 14.73, 15.38, 29.86, 39.77, 104.54, 110.31, 110.73, 111.16, 114.19, 119.61, 123.79, 126.32, 131.23, 138.08, 153.28, 178.48 ppm.

EXAMPLE 68 phenylene(t-butylcarboxamido)(2,5-dimethylcyclopentadienyl)titanium dimethyl

0.361 g (1.29 mmol) of TiCl₄ DME was melted in 16 mL of diethyl ether. Then, 1.61 mL of MeLi (1.6 M in diethyl ether) was added thereto at 0° C. and stirred for 15 minutes. Next, 0.400 g (1.29 mmol) of <C₆H₂(t-BuCON)(2,5-Me₂Cp)>Li₂ was added to the reaction product and stirred for 3 hours. The solvent contained in the resultant reaction product was removed, and then the product was filtered using 15 mL of pentane. The used pentane was removed thereby obtaining dark green solid. (0.320 g, 72%). The crystalline structure of the product is illustrated in FIG. 3.

¹H NMR (C₆D₆): δ 1.12 (s, 6H, Ti—CH₃), 1.36 (s, 9H, C(CH₃)₃), 1.62 (s, 6H, Cp-CH₃), 6.46 (s, 2H, Cp-H), 6.85 (td, J=7.2, 1.2 Hz, 1H, H^(4 or 5)), 6.98 (td, J=7.2, 1.2 Hz, 1H, H^(4 or 5)), 7.01-7.04 (m, 2H, H^(3 and 6)) ppm.

EXAMPLE 69 phenylene(t-butylcarboxamido)(2,3,5-trimethylcyclopentadienyl)titanium dimethyl

An experiment was performed in the same manner as in Example 68 using 0.331 g (1.18 mmol) of TiCl₄ DME, 1.48 ml of MeLi (1.6M in diethyl ether), and 0.400 g (1.18 mmol) of <C₆H₂(t-BuCON)(2,3,5-Me₃Cp)>Li₂ (0.320 g, 75%).

¹H NMR (C₆D₆): δ 0.95 (s, 3H, Ti—CH₃), 1.23 (s, 3H, Ti—CH₃), 1.36 (s, 9H, C(CH₃)₃), 1.51 (s, 3H, Cp-CH₃), 1.66 (s, 3H, Cp-CH₃), 2.16 (s, 3H, Cp-CH₃), 6.25 (s, 1H, Cp-H), 6.87 (t, J=7.2 Hz, 1H, H^(4 or 5)), 6.99 (t, J=8.4 Hz, 1H, H^(4 or 5)), 7.03 (d, J=8.0 Hz, 1H, H^(3 or 6)), 7.07 (d, J=8.0 Hz, 1H, H^(3 or 6)) ppm.

COMPARATIVE EXAMPLE 1 butylidene(2,5-dimethylcyclopentadienyl)(cyclopentadienyl)titanium dichloride

26.52 g (95.68 mmoL) of normal butyl lithium was added to 10.4 g (47.84 mmol) of 2-(1-cyclopenta-1,4-dienyl-butyl)-1,3-dimethyl-cyclopenta-1,3-diene melted in 60 mL of a cold tetrahydrofuran in a nitrogen atmosphere via schlenkline. Then, the reaction solution was stirred for 12 hours, dried in a reduced pressure to remove a third of the solvent, filtered, and then washed using hexane, thereby obtaining lithium salt compound with an yield of 95%. The obtained lithium salt (3.38 g) was melted in pyridine to decrease the temperature thereof to −30° C. Separatly, 1.5 g (8.7 mmol) of Ti(NMe₂)₂Cl₂ was melted in toluene and then the temperature of the resultant solution was decreased to the same temperature. Then, the prepared two solutions were quicly mixed and reacted for 20 minutes. The reaction product was dried to remove the solvent and filtered using pentane, thereby obtaining a titan compound that is substituted with a dimethyl amino group.

¹H NMR (pyridine-d₅): δ 6.33 (s, 1H, Cp-H), 6.32 (s, 1H, Cp-H), 6.14 (d, J=2.8 Hz, 1 H, Me₂Cp-H), 6.08 (d, J=2.8 Hz, 1 H, Me₂Cp-H), 5.22 (s, 1H, Cp-H), 5.03 (s, 1H, Cp-H), 3.61 (t, 1H, CHCH₂), 2.99 (d, J=8.4 Hz 12H, NCH₃), 1.95 (s, 3 H, CH₃), 1.82 (s, 3 H, CH₃), 1.47 (quartet, J=7.2 H, 3 H, CHCH₃) ppm.

The titan compound that is substituted with a dimethyl amino group was melted in 35 mL of pentane, and then 2 eq. of Me₂SiC₂ (2.11 mL) was added thereto. The reaction solution was reacted for 30 minutes. Then, the red color of the product disappeared and a solid was formed. Only the solid was collected, melted with benzene, and then left sat for 12 hours. The generated solid was filtered and the used solvent was revmoed, thereby obtaining a titan-containing bridged metallocene compound (Yield: 50%).

¹H NMR (C₆D₆): δ 6.77 (quartet, J=2.4 Hz, 1 H, Cp-H^(3 or 4)), 6.68 (m, 1 H, Cp-H^(3 or 4)), 6.67 (d, J=4 Hz, 1 H, Me₂Cp-H), 6.64 (d, J=4 Hz, 1 H, Me₂Cp-H), 5.19 (dd, J=3.2, 2.8 Hz, 1 H, Cp-H^(1 or 5)), 5.02 (dd, J=3.2, 2.8 Hz, 1 H, Cp-H^(1 or 5)), 3.62 (t, 1 H, bridge), 1.74 (s, 3 H, CH₃), 1.59 (s, 3 H, CH₃) ppm.

COMPARATIVE EXAMPLE 2 bis(n-butylcyclopentadienyl)zirconium dichloride

The zirconium metal compound was purchaced from US Boulder Scientific Co. and directly used for ethylene copolymerization.

COMPARATIVE EXAMPLE 3 iso-propylidene(cyclopentadienyl)(9-fluorenyl)zirconium dichloride

The zirconium metal compound was purchaced from US Boulder Scientific Co. and directly used for ethylene homopolymerization.

Ethylene Homopolymerization

EXAMPLE 70 Ethylene Homopolymerization in the Prescence of 1,2-C₆H₄(2,4,6-Me₃PhSO₂N)(2,5-Me₂Cp)TiCl₂

250 mL of toluene solvent was loaded to a 500 mL glass reactor. Then, 1.0 mol of the titanium compound that was treated with 25 mol of triisobutylaluminum compound, and 5.0 mol of trityl tetrakis(pentafluorophenyl)borate cocatalyst were sequentially added thereto. Right after the reactor was shaken in an oil bath at 90° C. for 2 minutes at a rate of 300 rpm, ethylene pressure (40 psig) was added to the reactor to perform polymerization at 90° C. for 5 minutes. The residual ethylene gas was removed. Then, excess ethanol was added to the reaction product to induce the polymer precipitation. The obtained polymer was washed with ethanol and acetone two to three times, respectively. The washed product was dried in an oven at 80° C. for 12 hours or more. The mass of the measured polymer was 3.26 g, and the degree of activity of the catalyst was 39.1 Kg PE/mmol-Ti hr.

EXAMPLE 71 Ethylene Homopolymerization in the Prescence of 1,2-C₆H₄(4-MePhSO₂N)(2,5-Me₂Cp)TiCl₂

Ethylene homopolymerization was performed in the same manner as in Example 70 using 1.0 mol of the titanium compound. The mass of the measured polymer was 1.10 g, and the degree of activity of the catalyst was 13.2 Kg PE/mmol-Ti hr.

EXAMPLE 72 Ethylene Homopolymerization in the Prescence of 1,2-C₆H₄(MeSO₂N)(2,5-Me₂Cp)TiCl₂

Ethylene homopolymerization was performed in the same manner as in Example 70 using 1.0 mol of the titanium compound. The mass of the measured polymer was 0.33 g, and the degree of activity of the catalyst was 4.0 Kg PE/mmol-Ti hr.

COMPARATIVE EXAMPLE 5 Ethylene Homopolymerization in the Prescence of H₃C(CH₂)₃CH(2,5-Me₂Cp)(Cp)TiCl₂

Ethylene homopolymerization was performed for 10 minutes in the same manner as in Example 70 using 2.5 mol of the titanium compound. The mass of the measured polymer was 2.25 g, and the degree of activity of the catalyst was 5.40 Kg PE/mmol-Ti hr.

Ethylene Copolymerization

EXAMPLE 73 Copolymerzation of Low-Pressure Ethylene and 1-octene

250 mL of toluene solvent and a proper amount of 1-octene were added to a 500 mL glass reactor. Then, a 1.0 micromole of a titanium compound that was treated with 25 micromole of triisobutylaluminum compound, and 5.0 micromole of trityl tetrakis(pentafluorophenyl)borate cocatalyst were sequentially added thereto. The reactor was placed in an oil bath at 90° C., and then 40 psig of ethylene pressure was added to the reactor to perform polymerization for 10 minutes. The residual ethylene gas was revmoed, and then excess ethanol was added to the reaction product to induce the polymer precipitation. The obtained polymer was washed with ethanol and acetone two to three times, respectively, and then dried at 80° C. for 12 hours or more.

EXAMPLE 74 Copolymerzation of High-Pressure Ethylene and 1-octene

1.0 L of toluene solvent and a proper amount of 1-octene were added to a 2 L autoclave reactor. Then, the reactor was preheated at 90° C. and at the same time, the ractor was filled with 6 bar of ethylene. 5.0 micromole of titanium compoud that was treated with 125 micromole of triisobutylaluminum compound, and 25 micromole of trityl tetrakis(pentafluorophenyl)borate cocatalyst were sequentially added to a 25 mL catalyst storage tank. At this time, 13 bar of ethylene was added to the catalyst storage tank to perform copolymerization for 10 minutes. The residual ethylene gas was removed, and then excess ethanol was added to the polymer solution to induce precipitation. The obtained polymer was washed with ethanol and acetone two to three times, respectively, and then dried at 80° C. for 12 hours or more.

EXAMPLE 75 Copolymerzation of High-Pressure Ethylene and 1-octene

1.0 L of toluene solvent and 1-octene (fixed at 0.8 M) were added to a 2 L autoclave reactor. Then, ethylene copolymerization was carried out in the same mmaner as in Example 74 using various titanium compounds (5.0 micromole).

EXAMPLE 76 Copolymerzation of High-Pressure Ethylene and 1-octene

1.0 L of hexane solvent and 1-octene (fixed at 0.8 M) were added to a 2 L autoclave reactor. Then, ethylene copolymerization was carried out in the same mmaner as in Example 74 using various titanium compounds (5.0 micromole) at 140° C. at an ethylene pressure of 35 bar.

Properties Measurement (Weight, Activity, Melt Index, Melting Point, and Density

A melt index (MI) of a polymer was measured using ASTM D-1238 (Condition E, 190° C., 2.16 Kg weight). A melting point (T_(m)) of the polymer was a Differential Scanning Calorimeter (DSC) 2920 produced by TA Co. That is, the DSC curve of the polymer was obtained by increasing the temperature to 200° C., maintaining at 200° C. for 5, decreasing to 30° C., and then increasing. The summit of the DSC curve corresponds to a melting point. At this time, the increase and decrease rates of the temperature were 10° C./min, and the melting point was obtained in a second temperature increase period.

In order to measure the density of the polymer, a sample that had been treated with 1,000 ppm of an antioxidant was formed into a sheet having a thickness of 3 mm and a diameter of 2 cm by a 180° C. press mold, and then the prepared sheet was cooled to 10° C./min. The cooled sheet was measured using a mettler scale.

EXPERIMENTAL EXAMPLE 1 Copolymerization of Ethylene and 1-octene

Various properties of copolymers prepared according to Example 73 using transition metal complexes prepared according to Examples 32, 35, and 39 and Comparative Example 1. The results are shown in Table 1. TABLE 1 Complex 1-octene Polymer Activity Melt Index^(a) Melting Branch Amount used (M) Weight (g) (Kg/mmol-Ti hr) (g/10 min) Point (° C.) (mol %) Example 32 0.1 2.3 13.8 19.5 89.5 89.5 Example 35 0.1 4.7 28.3 Not measurable 96.7 11 Example 35 0.3 2.0 12.0 Not measurable Not measurable 25 Example 39 0.1 0.57 3.2 Has not been measured Comparative 0.1 1.09 6.54 Has not been measured Example 1^(b) ^(a)I₂ value, ^(b)the weight average molecular weight (Mw) of a polymer obtained using a compex of Comparative Example 1 was 108,150

As shown in Table 1, a degree of copolymerization acitivty of the catlyst complexes synthesized in Examples 32, 35, and 39 is dependent on a substitutent of nitrogen. For example, the complex that was synthesized according to Example 35 in which p-toluenesulfonyl was introduced to nitrogen, showed high acitivty compared to other catalysts complexes having the same concentration of octane. Almost all of the complexes having a phenylene bridge accoridng to the present invention showed high copolymerization activity, and high reactivity to an olefin monomer having a large steric hindrance, such as 1-octene, compared to when the complex having biscyclopentadienyl of Comparative Example 1 was used.

EXPERIMENTAL EXAMPLE 2 Copolymerization of Ethylene and 1-octene

Properties of copolymers prepared accoridng to Example 74 using the transition metal complexes synthesized according to Examples 32, 35, and 39 were measured. The results are shown in Table 2. TABLE 2 1-octene Activity Melt Index^(a) Melting Point Density Complex used (M) (g/10 min) (g/10 min) (° C.) (g/cc) Example 32 0.3 34.4 6.8  108.9 0.915 Example 32 0.5 23.0 16.6  98.7 0.900 Example 32 0.8 16.8 Not measurable Not measurable Not measurable Example 35 0.1 55.1 3.02 121.7 0.934 Example 35  0.1^(b) 40.8 1.35 122.3 0.935 Example 35 0.3 50.8 3.70 107.7 0.912 Example 35 0.5 78.4 43    103.0 0.899 Example 35 0.8 87.2 103    89.8 0.883 Example 35 1.2 82.3 Not measurable Not measurable 0.865 Example 39 0.1 24.7 60.8^(c  ) 121.1 0.931 Example 39 0.3 24.2 4.1  110.0 0.915 Comparative 0.3 85.2 2.57 121.0 has not Example 1 been measured ^(a)I₂ value, ^(b)reaction temperature of 110° C., ^(c)I₂₁ value

As shown in Table 2, the complex prepared according to Example 35 showed higher copolymerization activity than other complexes, and an increase of the activity continued to some level as the concentration of octene increased. Almost all of the complexes showed low acitivty compared to the complex of Comparative Example 1, but a copolymer that was synthesized using the complexes to which a bridge is introduced accoridng to the present invention had lower density than when the complex having a bisphenylenecyclopentadienyl group of Comparative Example 1 was used, which indicates high reactivity of the complex according to the present invention with respect to an olefin monomer having a large steric hindrance, such as 1 -octene.

EXPERIMENTAL EXAMPLE 3 Copolymerization of Ethylene and 1-octene

Properties of copolymers prepared accoridng to Example 74 using the transition metal complexes synthesized according to Examples 35, 46-48, 61-64, and 69 and Comparative Examples 2 and 3 were measured. The results are shown in Table 3. TABLE 3 Polymer Activity Melt Melting Complex Mass (Kg/ Index^(a) Point Density used (g) mmol-Ti hr) (g/10 min) (° C.) (g/cc) Example 46 80.04 96.05 26 92.8 0.877 Example 47 3.39 4.07 2.70 Not 0.891 measurable Example 48 5.06 6.07 0.23 90.7 0.858 Example 61 7.06 8.47 0.14 112.9 0.879 Example 62 34.96 41.95 0.33 74.8 0.870 Example 63 44.01 52.81 3.85 Not 0.852 measurable Example 64 17.03 20.44 0.26 62.0 0.861 Example 69 55.70 66.84 0.64 63.4 0.872 Comparative 118.8 142.5 100 120.7 0.939 Example 2 Comparative 112.1 134.6 66.4 98.5 0.910 Example 3 ^(a)I₂ value

As shown in Talbe 3, the complexes in which t-butylcarbonyl(butylcarbonyl) was introduced to nitrogen prepared according to Examples 61 through 64, and 69 showed lower copolymerization activity than the complexes in which a sulfonyl group is introduced to a nitrogen prepared according to Exapmle 46. However, a polymer synthesized using the complexes in which t-butylcarbonyl(butylcarbonyl) was introduced to nitrogen prepared according to Examples 61 through 64, and 69 had high molecular weight. The catalyst complexes according to the present invention showed lower activity than the catalyst complexes of Comparative Example 2 and 3, but a copolymer that was synthesized using the catalyst complexes according to the present invention had higher molecular weight and higher polymer density of 0.860 g/cc. Thus, the catalyst complexes according to the present invention showed excellent copolymerization reactivity.

EXPERIMENTAL EXAMPLE 4 Copolymerization of Ethylene and 1-octene

Properties of copolymers prepared accoridng to Example 76 using the transition metal complexes synthesized according to Examples 46 and 69. The results are shown in Table 4. TABLE 4 Polymer Activity Melt Melting Complex mass (Kg/ Index^(a) Point Density used (g) mmol-Ti hr) (g/10 min) (° C.) (g/cc) Example 46 21.33 12.80 Has not been measured Example 69  28.89^(b) 11.56 Has not been measured ^(a)I₂ value, ^(b)polymerization for 15 minutes

As shown in Table 4, as a result of copolymerization at high temperature and high pressure, it was found that the catalyst complexes according to the present invention was stably used for copolyerization at high temperature of 140° C.

Compared to a conventional transition metal complex having a silicon bridge and an oxido ligand, a transition metal complex according to the present invention has a phenylene bridge, so that a monomer easily approaches the transition metal complex in terms of structure and a pentagon ring structure of the transition metal complex is stably maintained. By using a catalyst composition including the transition metal complex, a polyolefin copolymer having a very low density less than 0.910 g/cc can be obtained.

While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it will be understood by those of ordinary skill in the art that various changes in form and details may be made therein without departing from the spirit and scope of the present invention as defined by the following claims. 

1. A transition metal complex of Formula 1:

where R1 and R2 are each independently a hydrogen atom; a C1-C20 alkyl, aryl, or silyl radical; a C1-C20 alkenyl, alkylaryl, or arylalkyl radical; or a metalloid radical of Group 14 metal substituted with hydrocarbyl, wherein R1 and R2 can be connected by an alkylidine radical that contains a C1-C20 alkyl or aryl radical to form a ring; R4 is each independently a hydrogen atom; a halogen radical; or a C1-C20 alkyl or aryl radical, wherein two R4 can be connected to form a fused ring structure; R3 is a C1-C20 alkyl sulfonyl, aryl sulfonyl, or silyl sulfonyl radical; a C1-C20 alkyl carbonyl, aryl carbonyl, or silyl carbonyl radical; C1-C20 alkyl carboxy, or aryl carboxy radical; or C1-C20 alkyl phosphonyl, or aryl phosphonyl radical; M is a transition metal of Group 4; and Q1 and Q2 are each independently a halogen radical; a C1-C20 alkyl or aryl amido radical; a C1-C20 alkyl, alkenyl, aryl, alkylaryl, or arylalkyl radical; or a C1-C20 alkylidene radical.
 2. The transition metal complex of claim 1, being represented by Formula 14:

where R11 and R12 are each independently hydrogen atom; or C1-C20 alkyl, aryl, or silyl radical; R14 is each independently hydrogen atom; a C1-C20 alkyl radical; or halogen radical; Q3 and Q4 are each independently a halogen radical; C1-C20 alkyl, or aryl amido radical; or C1-C20 alkyl radical; M is a transition metal of Group 4; and

where Y is a carbon atom or a sulfur atom; R9 is a hydrogen atom; a C1-C20 alkyl, aryl, or silyl radical; or a C1-C20 alcoxy, or aryloxy radical; and when Y is the carbon atom, n is 1, and when Y is the sulfur atom, n is
 2. 3. The transition metal complex of claim 1, being represented by one of the formulae below:

where where R10 is a methyl radical, a tosyl radical, a mesityl radical, or a t-butyl radical; Q5 and Q6 are each independently a methyl radical, a dimethylamido radical, or a chloride radical.
 4. A transition metal complex of Formula 2:

where R1 and R2 are each independently a hydrogen atom; a C1-C20 alkyl, aryl, or silyl radical; a C1-C20 alkenyl, alkylaryl, or arylalkyl radical; or a metalloid radical of Group 14 metal substituted with hydrocarbyl, wherein R1 and R2 can be connected by an alkylidine radical that contains a C1-C20 alkyl or aryl radical to form a ring; R4 is each independently a hydrogen atom; a halogen radical; or a C1-C20 alkyl or aryl radical, wherein two R4 are connected to form a fused ring structure; M is a transition metal of Group 4; Q1 and Q2 are each independently a halogen radical; a C1-C20 alkyl or aryl amido radical; a C1-C20 alkyl, alkenyl, aryl, alkylaryl, or arylalkyl radical; or a C1-C20 alkylidene radical; G is an oxygen atom or a sulfur atom; and R5 is a hydrogen atom; a C1-C20 alkyl or aryl radical; or a C1-C20 alcoxy or aryloxy radical.
 5. A transition metal complex of Formula 3:

where R1 and R2 are each independently a hydrogen atom; a C1-C20 alkyl, aryl, or silyl radical; a C1-C20 alkenyl, alkylaryl, or arylalkyl radical; or a metalloid radical of Group 14 metal substituted with hydrocarbyl, wherein R1 and R2 can be connected by an alkylidine radical that contains a C1-C20 alkyl or aryl radical to form a ring; R4 is each independently a hydrogen atom; a halogen radical; or a C1-C20 alkyl or aryl radical, wherein two R4 can be connected to form a fused ring structure; R5 is a hydrogen atom; a C1-C20 alkyl or aryl radical; or a C1-C20 alcoxy or aryloxy radical; M is a transition metal of Group 4; Q1 and Q2 are each independently a halogen radical; a C1-C20 alkyl or aryl amido radical; a C1-C20 alkyl, alkenyl, aryl, alkylaryl, or arylalkyl radical; or a C1-C20 alkylidene radical; and G′ is an oxygen atom, a sulfur atom, or a substituted nitrogen group (—NR) where R is a C1-C20 alkyl or aryl radical.
 6. The transition metal complex of claim 4, being represented by Formula 16:

where R11 and R12 are each independently hydrogen atom; or C1-C20 alkyl, aryl, or silyl radical; R14 is each independently a hydrogen atom; a C1-C20 alkyl radical; or a halogen radical; Q3 and Q4 are each independently a halogen radical; a C1-C20 alkyl or aryl amido radical; or a C1-C20 alkyl radical; M and R5 are described in claim 5; and G″ is an oxygen atom, a sulfur atom, or a substituted nitrogen group where a subsituent is a C1-C20 alkyl or aryl amido radical.
 7. The transition metal complex of claim 4, being represented by one of the formulae below:

where R15 is a methyl radical, a t-butyl radical, or a t-butoxy radical; Q5 and Q6 are each independently a methyl radical, a dimethylamido radical, or a chloride radical; and X is a halogen radical.
 8. An amine-based compound of Formula 4:

where R1 and R2 are each independently a hydrogen atom; a C1-C20 alkyl, aryl, or silyl radical; a C1-C20 alkenyl, alkylaryl, or arylalkyl radical; or a metalloid radical of Group 14 metal substituted with hydrocarbyl, wherein R1 and R2 can be connected by an alkylidine radical that contains a C1-C20 alkyl or aryl radical to form a ring; R3 is a C1-C20 alkyl sulfonyl, aryl sulfonyl, or silyl sulfonyl radical; a C1-C20 alkyl carbonyl, aryl carbonyl, or silyl carbonyl radical; a C1-C20 alkyl carboxy, or aryl carboxy radical; or a C1-C20 alkyl phosphonyl, or aryl phosphonyl radical; and R4 is each independently a hydrogen atom; a halogen radical; or a C1-C20 alkyl or aryl radical, wherein two R4 can be connected to form a fused ring structure.
 9. An amine-based compound of Formula 5:

where R1 and R2 are each independently a hydrogen atom; a C1-C20 alkyl, aryl, or silyl radical; a C1-C20 alkenyl, alkylaryl, or arylalkyl radical; or a metalloid radical of Group 14 metal substituted with hydrocarbyl, wherein R1 and R2 can be connected by an alkylidine radical that contains a C1-C20 alkyl or aryl radical to form a ring; R3 is a C1-C20 alkyl sulfonyl, aryl sulfonyl, or silyl sulfonyl radical; a C1-C20 alkyl carbonyl, aryl carbonyl, or silyl carbonyl radical; a C1-C20 alkyl carboxy, or aryl carboxy radical; or a C1-C20 alkyl phosphonyl, or aryl phosphonyl radical; and R4 is each independently a hydrogen atom; a halogen radical; or a C1-C20 alkyl or aryl radical, wherein two R4 can be connected to form a fused ring structure.
 10. An amine-based compound of Formula 6:

where R1 and R2 are each independently a hydrogen atom; a C1-C20 alkyl, aryl, or silyl radical; a C1-C20 alkenyl, alkylaryl, or arylalkyl radical; or a metalloid radical of Group 14 metal substituted with hydrocarbyl, wherein R1 and R2 can be connected by an alkylidine radical that contains a C1-C20 alkyl or aryl radical to form a ring; R3 is a C1-C20 alkyl sulfonyl, aryl sulfonyl, or silyl sulfonyl radical; a C1-C20 alkyl carbonyl, aryl carbonyl, or silyl carbonyl radical; a C1-C20 alkyl carboxy, or aryl carboxy radical; or a C1-C20 alkyl phosphonyl, or aryl phosphonyl radical; and R4 is each independently a hydrogen atom; a halogen radical; or a C1-C20 alkyl or aryl radical, wherein two R4 can be connected to form a fused ring structure.
 11. An amine-based compound of Formula 7:

where R1 and R2 are each independently a hydrogen atom; a C1-C20 alkyl, aryl, or silyl radical; a C1-C20 alkenyl, alkylaryl, or arylalkyl radical; or a metalloid radical of Group 14 metal substituted with hydrocarbyl, wherein R1 and R2 can be connected by an alkylidine radical that contains a C1-C20 alkyl or aryl radical to form a ring; R3 is a C1-C20 alkyl sulfonyl, aryl sulfonyl, or silyl sulfonyl radical; a C1-C20 alkyl carbonyl, aryl carbonyl, or silyl carbonyl radical; a C1-C20 alkyl carboxy, or aryl carboxy radical; or a C1-C20 alkyl phosphonyl, or aryl phosphonyl radical; and R4 is each independently a hydrogen atom; a halogen radical; or a C1-C20 alkyl or aryl radical, wherein two R4 can be connected to form a fused ring structure.
 12. An organic ketone-based compound of Formula 8:

where R1 and R2 are each independently a hydrogen atom; a C1-C20 alkyl, aryl, or silyl radical; a C1-C20 alkenyl, alkylaryl, or arylalkyl radical; or a metalloid radical of Group 14 metal substituted with hydrocarbyl, wherein R1 and R2 can be connected by an alkyllidine radical that contains a C1-C20 alkyl or aryl radical to form a ring.
 13. A method of synthesizing a transition metal complex, the method comprising: synthesizing a compound of Formula 6 by reacting a boronic acid compound of Formula 8 with a 2-bromoaniline compound of Formula 9; synthesizing a compound of Formula 5 by the compound of Formula 6 with R3X where X is a halogen atom; synthesizing a compound of Formula 4 by reacting a compound of Formula 5 with R1 Li and then adding an acid thereto; and synthesizing a complex of Formula 1 or Formula 2 by reacting the comound of Formula 4 with the compound of Formula 10 and then adding (CH3)nSiX4-n where X is a halogen atom and n is 0, 1, 2, or 3 thereto:

where R4 is each independently a hydrogen atom; a halogen radical; or a C1-C20 alkyl or aryl radical, wherein two R4 are connected to form a fused ring structure; and M(N(R6)2)4   (10) where M is a transition metal of Group 4, and R6 is a C1-C20 alkyl or aryl radical.
 14. A method of synthesizing a transition metal complex, the method comprising: synthesizing a compound of Formula 6 by reacting a boronic acid compound of Formula 8 with a 2-bromoaniline compound of Formula 9; synthesizing a compound of Formula 7 by the compound of Formula 6 with R1Li and then adding an acid thereto; synthesizing a compound of Formula 4 by reacting a compound of Formula 7 with R3X where X is a halogen atom; and synthesizing a complex of Formula 1 or Formula 2 by reacting the comound of Formula 4 with the compound of Formula 10 and then adding (CH3)nSiX4-n where X is a halogen atom and n is 0, 1, 2, or 3 thereto.
 15. A method of synthesizing a transition metal complex, the method comprising: synthesizing a dilithium form of a compound of Formula 7 by reacting a compound of Formula 7 with an alkyllihtium that is a base; and synthesizing a complex of Formula 3 by reacting the dilithium compound and an in-situ compound of alkyllithium and MX4 where X is halogen and M is a transition metal of Group
 4. 16. A catalyst composition comprising: the transition metal complex of any one of formulae 1, 2, and 3; and at least one cocatalyst compound selected from compounds of Formulae 11 through 13: —[Al(R7)-O]a-   (11) where R7 is each independently a halogen radical; a C1-C20 hydrocarbyl radical; or a C1-C20 hydrocarbyl radical substituted with halogen; and a is an integer of 2 or greater; D(R7)3   (12) where D is aluminum or borone; and R7 is described above; and [L-H]+[Z(A)4]-, or [L]+[Z(A)4]-   (13) where L is a neutral or cationic Lewis acid; H is a hydrogen atom; Z is an element of Group 13; A is each independently a C6-C20 aryl or alkyl radical in which at least one hydrogen atom is substituted with halogen or a C1-C20 hydrocarbyl, alcoxy, or phenoxy radical.
 17. A method of preparing a catalyst composition, the method comprising: contacting the transition metal complex of any one of formulae 1, 2, and 3 with the compound of Formula 11 or Formula 12, thereby obtaining a mixture; and adding a compound of Formula 13 to the mixture.
 18. The method of claim 17, wherein the mole ratio of the transition metal complex to the compound of Formula 11 or Formula 12 is in the range of 1:2 through 1:5000 and the mole ratio of the transition metal complex of the compound of Formula 13 is in the range of 1:1 through 1:25.
 19. A method of synthesizing an olefin polymer, comprising contacting the catalyst composition of claim 16 with a monomer.
 20. The method of claim 19, wherein the monomer comprises at least one monomer selected from the group consisting of ethylene, propylene, 1-butene, 1-pentene, 4-methyl-1-pentene, 1-hexene, 1-hepthene, 1-octene, 1-decene, 1-undecene, 1-dodecene, 1-tetradecene, 1-hexadecene, and 1-itosen.
 21. An olefin polymer synthesized using the method of claim
 19. 22. The olefin polymer of claim 21, wherein the monomer comprises: ethylene; and, at least one compound selected from the group consisting of propylene, 1-butene, 1-hexene, 4-methyl-1-pentene, and 1-octene.
 23. The transition metal complex of claim 5, being represented by Formula 16:

where R11 and R12 are each independently hydrogen atom; or C1-C20 alkyl, aryl, or silyl radical; R14 is each independently a hydrogen atom; a C1-C20 alkyl radical; or a halogen radical; Q3 and Q4 are each independently a halogen radical; a C1-C20 alkyl or aryl amido radical; or a C1-C20 alkyl radical; M and R5 are described in claim 5; and G″ is an oxygen atom, a sulfur atom, or a substituted nitrogen group where a subsituent is a C1-C20 alkyl or aryl amido radical.
 24. The transition metal complex of claim 5, being represented by one of the formulae below:

where R15 is a methyl radical, a t-butyl radical, or a t-butoxy radical; Q5 and Q6 are each independently a methyl radical, a dimethylamido radical, or a chloride radical; and X is a halogen radical.
 25. An olefin polymer synthesized using the method of claim
 20. 